    Enhanced Optoelectronic Properties of Magnetron Sputtered Ito/Ag Multilayers by Electro-Annealing
    (AVS, 2022) Uyanık, Zemzem; Türkoğlu, Fulya; Köseoğlu, Hasan; Ekmekçioğlu, Merve; Ata, Bengü; Demirhan, Yasemin; Özdemir, Mehtap; Aygün, Gülnur; Özyüzer, Lütfi
    Indium tin oxide/silver/indium tin oxide (ITO/Ag/ITO) multilayers have attracted much attention to fulfill the growing need for high-performance transparent conducting oxide electrodes. To make these transparent multilayers work better, electro-annealing, which is a method of self-heating by electric current, can be effective. Moreover, the effect of current on ITO/Ag/ITO multilayers should be investigated to make sure that electronic devices will be reliable over their lifetime. In this study, ITO/Ag/ITO multilayer electrodes with varying Ag thicknesses were grown by DC magnetron sputtering at room temperature. Structural, optical, and electrical properties of these multilayers were investigated before and after electro-annealing. Measurement results revealed that improved optical transmittance and sheet resistance can be obtained by the optimization of Ag thickness for the as-grown ITO/Ag/ITO layers. The highest figure of merit (FoM) value of 17.37 × 10−3 Ω−1 with optical transmittance of 85.15% in the visible region and sheet resistance of 11.54 Ω/□ was obtained for the Ag thickness of 16.5 nm for as-grown samples. The electro-annealing of as-grown ITO/Ag/ITO multilayers led to improved optical behavior of the multilayer structure over a wide spectral range, especially in the near-infrared range. Electro-annealing also provided an improvement in the crystallinity and sheet resistance of the electrodes. The improvement of the electrical and optical properties of the structure enabled a FoM of 23.07 × 10−3 Ω−1 with the optical transmittance of 86.80% in the visible region and sheet resistance of 10.52 Ω/□. The findings of this work provide proper knowledge of the properties of ITO/Ag/ITO multilayers under electrical current and suggest that the overall performance of the multilayers can be improved by the electro-annealing process.
  • Article
    Citation - WoS: 2
    Citation - Scopus: 2
    Enhancing the Photo-Response Characteristics of Graphene/N-si Based Schottky Barrier Photodiodes by Increasing the Number of Graphene Layers
    (AVS, 2022) Fidan, Mehmet; Ünverdi, Özhan; Çelebi, Cem
    The impact of the number of graphene layers on the spectral responsivity and response speed of graphene/n-type Si (Gr/n-Si)-based Schottky barrier photodiodes is investigated. Gr/n-Si photodiode devices are fabricated by transferring chemical vapor deposition-grown graphene layers one by one on n-Si substrates, reaching up to three graphene layers. The devices show a clear rectifying Schottky character and have a maximum responsivity at a peak wavelength of 905 nm. Wavelength-resolved and time-dependent photocurrent measurements demonstrated that both spectral responsivity and response speed are enhanced as the number of graphene layers is increased from 1 to 3 on n-Si substrates. For example, the spectral responsivity and the response speed of the fabricated device were found to be improved by about 15% (e.g., from 0.65 to 0.75 AW-1) and 50% (e.g., 14 to 7 μs), respectively, when three graphene layers are used as the hole-collecting cathode electrode. The experimentally obtained results showed that the device parameters, such as spectral responsivity and response speed of Gr/n-Si Schottky barrier photodiodes, can be boosted simply by increasing the number of graphene layers on n-Si substrates.