Physics / Fizik
Permanent URI for this collectionhttps://hdl.handle.net/11147/6
Browse
4 results
Search Results
Other Erratum To: Mbe-Grown Cdte Layers on Gaas With In-Assisted Thermal Deoxidation(Springer Verlag, 2016) Arı, Ozan; Bilgilisoy, Elif; Özçeri, Elif; Selamet, YusufArticle Citation - WoS: 6Citation - Scopus: 5Mbe-Grown Cdte Layers on Gaas With In-Assisted Thermal Deoxidation(Springer Verlag, 2016) Arı, Ozan; Bilgilisoy, Elif; Özçeri, Elif; Selamet, YusufMolecular beam epitaxy (MBE) growth of thin (∼2 μm) CdTe layers characterized by high crystal quality and low defect density on lattice mismatched substrates, such as GaAs and Si, has thus far been difficult to achieve. In this work, we report the effects of in situ thermal deoxidation under In and As4 overpressure prior to the CdTe growth on epiready GaAs(211)B wafers, aiming to enhance CdTe crystal quality. Thermally deoxidized GaAs samples were analyzed using in situ reflection high energy electron diffraction, along with ex situ x-ray photo-electron spectroscopy (XPS) and atomic force microscopy. MBE-grown CdTe layers were characterized using x-ray diffraction (XRD) and Everson-type wet chemical defect decoration etching. We found that In-assisted desorption allowed for easier surface preparation and resulted in a smoother surface compared to As-assisted surface preparation. By applying In-assisted thermal deoxidation to GaAs substrates prior to the CdTe growth, we have obtained single crystal CdTe films with a CdTe(422) XRD rocking curve with a full-width half-maximum value of 130.8 arc-s and etch pit density of 4 × 106 cm−2 for 2.54 μm thickness. We confirmed, by XPS analysis, no In contamination on the thermally deoxidized surface.Article Citation - WoS: 10Citation - Scopus: 11The Effects of Sb Substitution on Structural Properties in Yba 2cu 3o 7 Superconductors(Springer Verlag, 2011) Akyüz, Gönül B.; Kocabaş, Kemal; Yıldız, Aylin; Özyüzer, Lütfi; Çiftçioglu, MuhsinIn this study, the effects of partial Sb 3+ ion substitutions for the Y sites and the Cu sites on the superconducting properties of YBa 2Cu 3O y (Y123) ceramic superconductors were investigated. The samples were prepared by the conventional solid-state reaction method and the properties of the samples were investigated by means of X-ray diffraction, AC magnetic susceptibility measurements, scanning electron microscope, and energy dispersive X-ray analysis. The critical temperatures were determined to be in the range of 80-92 K for both Systems I and II. It was found that Sb-addition leads to the formation of the non-superconducting YBa 2SbO 6 phase, which has a negative effect on the critical temperature, since the highest critical temperature was measured for pure Y123. However, the increasing substitution level has a negligible effect on the X-ray diffraction analysis peak intensities of the superconducting phases. In addition, SEM images showed that Sb substitution decreases the grain size and modifies the microstructure development, which makes the samples denser.Article Citation - WoS: 89Citation - Scopus: 94Effects of Li Substitution in Bi-2223 Superconductors(Springer Verlag, 2008) Bilgili, Özlem; Selamet, Yusuf; Kocabaş, KemalThe effects of Li substitution on the properties of high temperature superconductor Bi 17Pb 0.3Sr 2C 2Cu 3-x Li x O y were investigated. The samples were prepared by substituting Li (x=0.00-0.20) with changing ratios by a solid state reaction method. The samples were characterized by X-ray diffraction, DC electrical resistivity, AC magnetic susceptibility, and scanning electronic microscopy (SEM). The X-ray diffraction studies were done at room temperature and the lattice constants of the material were determined by indexing all the peaks observed. This study shows that there are two coexisting phases; high-T c (2223) phase and low-T c (2212) phase. The lattice structure of the material belongs to the orthorhombic unit cell. The volume fraction was estimated from the intensities of Bi-(2223) and Bi-(2212) phases. The sample with 20 wt% of added Li showed the higher volume fraction of Bi-(2223) phase formed (81%) compared to the other samples. The DC electrical resistivity of all the samples decreased as the wt% of Li increased. Both the onset critical temperatures T c (onset) and zero electrical resistivity critical temperatures T c (R=0) of the samples were determined from the DC electrical resistivity measurements. The observed value of the onset critical T c (onset) temperature was 110 K agreeing well with the magnetic susceptibility measurements. We obtained T c onset at 112 K from AC magnetic susceptibility measurements. © 2008 Springer Science+Business Media, LLC.