  • Article
    Citation - WoS: 5
    Citation - Scopus: 5
    Effect of the Synthesis Conditions on the Properties of Co Embedded Porous Si Nanostructures
    (Elsevier Ltd., 2019) Çetinel, Alper; Artunç, Nurcan; Tarhan, Enver
    The electrodeposition of cobalt in the porous silicon (PSi) substrate was investigated in terms of the deposition times and current densities. The PSi/Co samples were characterized by SEM, XRD, Raman, and photoluminescence (PL) spectroscopies. The results indicated that for all current densities, the PL intensities of PSi/Co samples with shorter deposition times (t(s) <= 20 min) increased due to spherical Co nanoparticles (NPs) could be created the new recombination centers, compared to that of the undeposited PSi. On the other hand, the PL intensity of PSi/Co samples significantly decreased at longer deposition times (t(1) > 20 min) because of larger Co NP cluster promoted the formation of non-radiative centers. The increased PL intensities in samples with t(s) were attributed to both the quantum confinement effect and surface effects. PL analyses also suggested that after exposure to air for 60 days, PL characteristics of PSi/Co were stabilized depending on deposition time and current density.
  • Article
    Citation - WoS: 8
    Citation - Scopus: 8
    Influence of Applied Current Density on the Nanostructural and Light Emitting Properties of N-Type Porous Silicon
    (World Scientific Publishing Co. Pte Ltd, 2015) Çetinel, A.; Artunç, N.; Şahin, Gündoğdu; Tarhan, Enver
    Effects of current density on nanostructure and light emitting properties of porous silicon (PS) samples were investigated by field emission scanning electron microscope (FE-SEM), gravimetric method, Raman and photoluminescence (PL) spectroscopy. FE-SEM images have shown that below 60 mA/cm2, macropore and mesopore arrays, exhibiting rough morphology, are formed together, whose pore diameter, pore depth and porosity are about 265-760 nm, 58-63 μ m and 44-61%, respectively. However, PS samples prepared above 60 mA/cm2 display smooth and straight macropore arrays, with pore diameter ranging from 900-1250 nm, porosity of 61-80% and pore depth between 63-69 μm. Raman analyses have shown that when the current density is increased from 10 mA/cm2 to 100 mA/cm2, Raman peaks of PS samples shift to lower wavenumbers by comparison to crystalline silicon (c-Si). The highest Raman peak shift is found to be 3.2 cm-1 for PS sample, prepared at 90 mA/cm2, which has the smallest nanocrystallite size, about 5.2 nm. This sample also shows a pronounced PL, with the highest blue shifting, of about 12 nm. Nanocrystalline silicon, with the smallest nanocrystallite size, confirmed by our Raman analyses using microcrystal model (MCM), should be responsible for both the highest Raman peak shift and PL blue shift due to quantum confinement effect (QCE).