Environmental Engineering / Çevre Mühendisliği
Permanent URI for this collectionhttps://hdl.handle.net/11147/4321
Browse
2 results
Search Results
Article Citation - WoS: 20Citation - Scopus: 24Lime-Activated One-Part Geopolymer Mortars From Construction, Demolition and Industrial Wastes(Elsevier, 2024) Kogbara, Reginald B.; Al-Zubi, Abdelrahman; Mortada, Youssef; Hammoud, Ahmad; Masad, Eyad A.; Khraisheh, Marwan K.This work focused on the production of one-part geopolymer mortars from construction and demolition wastes (CDW) blended with steel slag. Previous related studies on geopolymer production from CDW utilized conventional two-part geopolymers comprised of highly alkaline activator solutions and CDW materials. Thus, the study's significance consists in producing high-strength (≥35 MPa) ambient-cured mortars from CDW with predominantly concrete waste by replacing conventional highly alkaline activator solutions with an environmentally-friendly alkaline activator, Ca(OH)2 powder. Four mortar mixtures were produced with CDW contents ranging from 50 to 65 % dry weight, varying the brick waste content from 3 to 18 %. The effect of elevated temperature (40 °C) curing was also considered. The results showed that 55 % CDW content had optimum performance across all parameters studied such as compressive and flexural strengths, setting time, as well as changes in nuclear magnetic resonance (NMR)-determined pore structure (porosity and mean pore size) and x-ray diffraction (XRD)-determined degree of crystallinity over time. It had 28-day compressive and flexural strengths of 42 and 5.8 MPa, respectively, and initial and final setting times of 25 and 50 min. The importance of sufficient brick waste content in the geopolymer mixtures for effective mechanical performance is highlighted. The inclusion of concrete waste in powder form reduced compressive strength under ambient curing but improved performance at 40 °C curing. It is concluded that sustainable structural mortars can be produced by ‘just adding water’ to an optimized CDW mixture with predominantly concrete waste blended with brick waste and slag and activated by powdered Ca(OH)2. © 2023 The AuthorsArticle Citation - WoS: 17Citation - Scopus: 19Development of Ca(oh)2-Based Geopolymer for Additive Manufacturing Using Construction Wastes and Nanomaterials(Elsevier, 2023) Mortada, Youssef; Masad, Eyad; Kogbara, Reginald B.; Mansoor, Bilal; Seers, Thomas; Hammoud, Ahmad; Karaki, AymanRecent growth in additive manufacturing (AM) or 3D printing in the construction field has motivated the development of various materials that vary in its composition and properties. This paper introduces, characterizes, and evaluates the performance of a sustainable and environmentally friendly geopolymer mixture composed of construction wastes. The geopolymer mixture has calcium hydroxide (Ca(OH)2) as the main alkaline activator and incorporates nanomaterials such as nano-silica and nano-clay to enhance its suitability for AM. The combined use of Ca(OH)2 for alkali activation, and nanomaterials for tailoring the behavior of construction wastes for 3D printing, is novel and addresses the shortcomings of conventional alkaline activators. The paper includes the outcomes of the analysis of the mechanical properties, printability, and microstructure of the geopolymer mixture. The 28-day compressive strength of the mixture reached 42 MPa with ambient temperature curing, which is comparable to traditional geopolymers. The inclusion of 1 wt % of nano-silica accelerated the geopolymerization process and led to the largest (35 %) reduction in the setting time. Similarly, incorporating 1 wt % of nano-clay led to reduction of the thermal conductivity from 0.709 W/mK to 0.505 W/mK, due to the introduction of thermal barriers. The printability of the studied waste-based geopolymer mixture was validated through the successful fabrication of a 3D-printed model. © 2023 The Authors