Mechanical Engineering / Makina Mühendisliği
Permanent URI for this collectionhttps://hdl.handle.net/11147/4129
Browse
3 results
Search Results
Article Citation - WoS: 13Citation - Scopus: 14The Quasi-Static Crush Response of Electron-Beam Ti6al4v Body-Centred Lattices: The Effect of the Number of Cells, Strut Diameter and Face Sheet(Wiley, 2022) Güden, Mustafa; Alpkaya, Alican Tuncay; Arslan Hamat, Burcu; Hızlı, Burak; Taşdemirci, Alper; Tanrıkulu, A. Alptuğ; Yavaş, HakanThe effect of the number of cells, strut diameter and face sheet on the compression of electron-beam-melt (EBM) Ti6Al4V (Ti64) body-centred-cubic (BCC) lattices was investigated experimentally and numerically. The lattices with the same relative density (~0.182) were fabricated with and without 2-mm-thick face sheets in 10 and 5 mm cell size, 8–125 unit cell (two to five cells/edge) and 2 and 1 mm strut diameter. The experimental compression tests were further numerically simulated in the LS-DYNA. Experimentally two bending-dominated crushing modes, namely, lateral and diagonal layer crushing, were determined. The numerical models however exhibited merely a bending-dominated lateral layer crushing mode when the erosion strain was 0.4 and without face-sheet models showed a diagonal layer crushing mode when the erosion strain was 0.3. Lower erosion strains promoted a diagonal layer crushing mode by introducing geometrical inhomogeneity to the lattice, leading to strain localisation as similar to the face sheets which introduced extensive strut bending in the layers adjacent to the face sheets. The face-sheet model showed a higher but decreasing collapse strength at an increasing number of cells, just as opposite to the without face-sheet model, and the collapse strength of both models converged when the number of cells was higher than five-cell/edge. The decrease/increase of the collapse strengths of lattices before the critical number of cells was claimed mainly due to the size-imposed lattice boundary condition, rather than the specimen volume. The difference in the experimental collapse strengths between the 5- and the 10-mm cell-size lattices was ascribed to the variations in the microstructures—hence the material model parameters between the small-diameter and the large-diameter EBM-Ti64 strut lattices.Article Citation - WoS: 19Citation - Scopus: 19Experimental Investigation of Interaction Effects in Foam-Filled Thin-Walled Aluminum Tubes(Springer Verlag, 2006) Güden, Mustafa; Toksoy, Ahmet Kaan; Kavi, HalitThe interaction coefficients of polystyrene foam filling of thin-walled aluminum cylindrical tubes were investigated experimentally through compression testing of partially foam-filled tubes with and without adhesive. The experimental load-displacement curves and observation of the crushed sections of filled tubes have shown that partial foam filling reduced the fold length and hence increased the average crushing loads of tubes, proving the interaction effect between tube wall and filler. The interaction coefficients for the partial foam filling were further calculated to be in the level and/or higher than that of the foam plateau load of transverse direction.Article Citation - WoS: 37Citation - Scopus: 42Effects of Compaction Pressure and Particle Shape on the Porosity and Compression Mechanical Properties of Sintered Ti6al4v Powder Compacts for Hard Tissue Implantation(John Wiley and Sons Inc., 2007) Güden, Mustafa; Çelik, Emrah; Hızal, Alpay; Altındiş, Mustafa; Çetiner, SinanSintered Ti6Al4V powder compacts potentially to be used in implant applications were prepared using commercially available spherical and angular powders (100-200 mum) within the porosity range of 34-54%. Cylindrical green powder compacts were cold compacted at various pressures and then sintered at 1200 degrees C for 2 h. The final percent porosity and mean pore sizes were determined as functions of the applied compaction pressure and powder type. The mechanical properties were investigated through compression testing. Results have shown that yield strength of the powder compacts of 40-42% porosity was comparable with that of human cortical bone. As compared with previously investigated Ti powder compacts, Ti6Al4V powder compacts showed higher strength at similar porosity range. Microscopic observations on the failed compact samples revealed that failure occurred primarily by the separation of interparticle bond regions in the planes 45 degrees to the loading axis. Effects of compaction pressure and particle shape on the porosity and compression mechanical properties of sintered Ti6Al4V powder compacts for hard tissue implantation.