Mechanical Engineering / Makina Mühendisliği
Permanent URI for this collectionhttps://hdl.handle.net/11147/4129
Browse
3 results
Search Results
Now showing 1 - 3 of 3
Article Citation - WoS: 7Citation - Scopus: 7Investigating the Effects of Pa66 Electrospun Nanofibers Layered Within an Adhesive Composite Joint Fabricated Under Autoclave Curing(American Chemical Society, 2023) Esenoğlu, Gözde; Tanoğlu, Metin; Barışık, Murat; İplikçi, Hande; Yeke, Melisa; Nuhoğlu, Kaan; Türkdoğan, Ceren; Martin, Seçkin; Aktaş, Engin; Dehneliler, Serkan; Gürbüz, Ahmet Ayberk; İriş, Mehmet ErdemEnhancing the performance of adhesively joined composite components is crucial for various industrial applications. In this study, polyamide 66 (PA66) nanofibers produced by electrospinning were coated on unidirectional carbon/epoxy prepregs to increase the bond strength of the composites. Carbon/epoxy prepregs with/without PA66 nanofiber coating on the bonding region were fabricated using the autoclave, which is often used in the aerospace industry. The single lap shear Charpy impact energy and Mode-I fracture toughness tests were employed to examine the effects of PA66 nanofibers on the mechanical properties of the joint region. Scanning electron microscopy (SEM) was used to investigate the nanofiber morphology and fracture modes. The thermal characteristics of Polyamide 66 nanofibers were explored by using differential scanning calorimetry (DSC). We observed that the electrospun PA66 nanofiber coating on the prepreg surfaces substantially improves the joint strength. Results revealed that the single lap shear and Charpy impact strength values of the composite joint are increased by about 79 and 24%, respectively, by coating PA66 nanofibers onto the joining region. The results also showed that by coating PA66 nanofibers, the Mode-I fracture toughness value was improved by about 107% while the glass transition temperature remained constant.Article Citation - WoS: 39Citation - Scopus: 40Mode-I Fracture Toughness of Carbon Fiber/Epoxy Composites Interleaved by Aramid Nonwoven Veils(Techno Press, 2019) Beylergil, Bertan; Tanoğlu, Metin; Aktaş, EnginIn this study, carbon fiber/epoxy (CF/EP) composites were interleaved with aramid nonwoven veils with an areal weight density of 8.5 g/m(2) to improve their Mode-I fracture toughness. The control and aramid interleaved CF/EP composite laminates were manufactured by VARTM in a [0]4 configuration. Tensile, three-point bending, compression, interlaminar shear, Charpy impact and Mode-I (DCB) fracture toughness values were determined to evaluate the effects of aramid nonwoven fabrics on the mechanical performance of the CF/EP composites. Thermomechanical behavior of the specimens was investigated by Dynamic Mechanical Analysis (DMA). The results showed that the propagation Mode-I fracture toughness values of CF/EP composites can be significantly improved (by about 72%) using aramid nonwoven fabrics. It was found that the main extrinsic toughening mechanism is aramid microfiber bridging acting behind the crack-tip. The incorporation of these nonwovens also increased interlaminar shear and Charpy impact strength by 10 and 16.5%, respectively. Moreover, it was revealed that the damping ability of the composites increased with the incorporation of aramid nonwoven fabrics in the interlaminar region of composites. On the other hand, they caused a reduction in in-plane mechanical properties due to the reduced carbon fiber volume fraction, increased thickness and void formation in the composites.Article Citation - WoS: 97Citation - Scopus: 110Effect of Polyamide-6,6 (pa 66) Nonwoven Veils on the Mechanical Performance of Carbon Fiber/Epoxy Composites(Elsevier Ltd., 2018) Beylergil, Bertan; Tanoğlu, Metin; Aktaş, EnginIn this study, carbon fiber/epoxy (CF/EP) composites were interleaved with polyamide-6,6 (PA 66) nonwoven veils at two different areal weight densities (17 and 50 gsm) to improve their delamination resistance against Mode-I loading. Mode-I fracture toughness (DCB), tensile, open hole tensile (OHT), flexural, compression, short beam shear (ILSS) and Charpy-impact tests were performed on the reference and PA 66 interleaved composite specimens. The DCB test results showed that the initiation and propagation Mode-I fracture toughness values of the composites were significantly improved by 84 and 171% using PA 66-17 gsm veils respectively, as compared to reference laminates. The use of denser PA 66-50 gsm veils in the interlaminar region led to higher improvement in fracture toughness values (349% for initiation and 718% for propagation) due to the higher amount of veil fibers involved in fiber bridging toughening mechanism. The incorporation of PA 66-50 gsm nonwoven veils also increased the ILSS and Charpy impact strength of the composites by 25 and 15%, respectively. On the other hand, the PA 66 veils reduced in-plane mechanical properties of CF/EP composites due to lower carbon fiber volume fraction and increased thickness.