Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7148
Browse
4 results
Search Results
Article Citation - WoS: 21Citation - Scopus: 24Development and Mechanical Behavior of Fml/Aluminium Foam Sandwiches(Springer Verlag, 2013) Baştürk, Suat Bahar; Tanoğlu, MetinIn this study, the Fiber-Metal Laminates (FMLs) containing glass fiber reinforced polypropylene (GFPP) and aluminum (Al) sheet were consolidated with Al foam cores for preparing the sandwich panels. The aim of this article is the comparison of the flexural properties of FML/Al foam sandwich panels bonded with various surface modification approaches (silane treatment and combination of silane treatment with polypropylene (PP) based film addition). The FML/foam sandwich systems were fabricated by laminating the components in a mould at 200 A degrees C under 1.5 MPa pressure. The energy absorbtion capacities and flexural mechanical properties of the prepared sandwich systems were evaluated by mechanical tests. Experiments were performed on samples of varying foam thicknesses (8, 20 and 30 mm). The bonding among the sandwich components were achieved by various surface modification techniques. The Al sheet/Al foam sandwiches were also consolidated by bonding the components with an epoxy adhesive to reveal the effect of GFPP on the flexural performance of the sandwich structures.Article Citation - WoS: 8Citation - Scopus: 8The Effect of Single-Walled Carbon Nanotube (swcnt) Concentration on the Mechanical and Rheological Behavior of Epoxy Matrix(Springer Verlag, 2020) Ay, Z.; Tanoğlu, MetinThe improvement of Mode I fracture toughness of epoxy by the addition of single-walled carbon nanotubes (SWCNTs) is considered. To prepare nanocomposites, chemical-vapor-deposition-grown SWCNTs noncovalently functionalized with an ethoxylated alcohol was used as the additive and a diglycidyl ether of bisphenol-A-based epoxy as the matrix material. The SWCNTs were dispersed in the epoxy matrix via a mechanical stirrer and a 3-roll mill. The effect of their concentration (0.0125, 0.025, 0.05, 0.1, 0.3, and 0.5 wt.%) on the mechanical properties of the nanocomposites was investigated, and the optimum concentration was determined. Mode I fracture toughness (single-edge-notch 3-point bending) and tensile tests were carried out on neat epoxy and SWCNT-reinforced epoxy nanocomposites. The fractured surfaces of fracture toughness and tensile test specimens were examined by the SEM to reveal the effect of SWCNTs on their failure modes.Article Citation - WoS: 39Citation - Scopus: 40Mode-I Fracture Toughness of Carbon Fiber/Epoxy Composites Interleaved by Aramid Nonwoven Veils(Techno Press, 2019) Beylergil, Bertan; Tanoğlu, Metin; Aktaş, EnginIn this study, carbon fiber/epoxy (CF/EP) composites were interleaved with aramid nonwoven veils with an areal weight density of 8.5 g/m(2) to improve their Mode-I fracture toughness. The control and aramid interleaved CF/EP composite laminates were manufactured by VARTM in a [0]4 configuration. Tensile, three-point bending, compression, interlaminar shear, Charpy impact and Mode-I (DCB) fracture toughness values were determined to evaluate the effects of aramid nonwoven fabrics on the mechanical performance of the CF/EP composites. Thermomechanical behavior of the specimens was investigated by Dynamic Mechanical Analysis (DMA). The results showed that the propagation Mode-I fracture toughness values of CF/EP composites can be significantly improved (by about 72%) using aramid nonwoven fabrics. It was found that the main extrinsic toughening mechanism is aramid microfiber bridging acting behind the crack-tip. The incorporation of these nonwovens also increased interlaminar shear and Charpy impact strength by 10 and 16.5%, respectively. Moreover, it was revealed that the damping ability of the composites increased with the incorporation of aramid nonwoven fabrics in the interlaminar region of composites. On the other hand, they caused a reduction in in-plane mechanical properties due to the reduced carbon fiber volume fraction, increased thickness and void formation in the composites.Article Citation - WoS: 23Citation - Scopus: 26Experimental and Statistical Analysis of Carbon Fiber/Epoxy Composites Interleaved With Nylon 6,6 Nonwoven Fabric Interlayers(SAGE Publications Inc., 2020) Beylergil, Bertan; Tanoğlu, Metin; Aktaş, EnginThermoplastic interleaving is a promising technique to improve delamination resistance of laminated composites. In this study, plain-weave carbon fiber/epoxy composites were interleaved with nylon 6,6 nonwoven fabrics with an areal weight density of 17 gsm. The carbon fiber/epoxy composite laminates with/without nylon 6,6 nonwoven fabric interlayers were manufactured by VARTM technique. Double cantilever beam fracture toughness tests were carried out on the prepared composite test specimens in accordance with ASTM 5528 standard. The experimental test data were statistically analyzed by two-parameter Weibull distribution. The results showed that the initiation and propagation fracture toughness Mode-I fracture toughness of carbon fiber/epoxy composites could be improved by about 34 and 156% (corresponding to a reliability level of 0.50) with the incorporation of nylon 6,6 interlayers in the interlaminar region, respectively. The results also revealed that the percent increase in the propagation fracture toughness value was 67 and 41% at reliability levels of 0.90 and 0.95, respectively.