Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7148
Browse
6 results
Search Results
Article Citation - WoS: 56Citation - Scopus: 63Processing, Characterization and Photocatalytic Properties of Cu Doped Tio2 Thin Films on Glass Substrate by Sol-Gel Technique(Elsevier Ltd., 2006) Çelik, Erdal; Gökçen, Z.; Azem, N. Funda Ak; Tanoğlu, Metin; Emrullahoğlu, O. F.The present paper describes processing, properties and photocatalytic application of Cu doped TiO2 thin films on glass substrate. Cu doped TiO2 coatings were successfully prepared on glass slide substrates using sol-gel method. The obtained solutions exhibit acidic characteristics. The phase structure, thermal, microstructure and surface properties of the coatings were characterized by using XRD, DTA/TG, SEM and AFM. Their adhesion properties and spectroscopic analysis were investigated by a scratch tester and UV-vis spectroscopy. Four different solutions were prepared by changing Cu/Ti ratios. Glass substrates were coated by solutions of Ti-alkoxide, Cu-chloride, glacial acetic acid and isopropanol. The obtained gel films were dried at 300 degrees C for 10 min and subsequently heat-treated at 500 degrees C for 5 min in air. The oxide thin films were annealed at 600 degrees C for 60min in air. TiO2, CuO, Cu4Ti, Ti3O5 and Cu3TiO4 phases were found in the coating. The organic matters were burned at temperatures between 200 and 350 degrees C and TiO2 crystallization was formed at 450 degrees C. The weight loss of the powder during process up to 600 degrees C is approximately 70%. The microstructural observations demonstrated that CuO content was led an improved surface morphology while thickness of the film and surface defects were increased in accordance with number of dipping. According to AFM results, it was found that as the Cu/Ti content increases the surface roughness of the films increases. In addition structural, thermal and microstructural results, it was found that the films of 0.73 ratio have better adhesion strength to the glass substrate among other coatings. The oxide films were found to be active for photocatalytic decomposition of metylene blue. (c) 2006 Published by Elsevier B.V.Article Citation - WoS: 15Citation - Scopus: 12Solubility and Aging of Lead Magnesium Niobate in Water(Elsevier Ltd., 2009) Şakar-Deliormanlı, Aylin; Çelik, Erdal; Polat, MehmetLead magnesium niobate (PMN) is an important relaxor ferroelectric material commonly employed in multilayer capacitor and actuator manufacturing owing to its high dielectric constant and superior electrostrictive properties. However, stability of this material in water is not very well known and there is need for a detailed investigation. In this research, solubility of lead magnesium niobate powders in water was determined as a function of solids concentration. The obtained results showed that the amount of cation leaching from the PMN surface depends on the pH value of the suspension and the solids concentration. The Pb2+ and Mg2+ ion dissolution was very high especially in the acidic pH range. Nevertheless, neither the dissolution mechanism nor the effects of dissolved ions on the stability were the same for those ions. The study provides new aspects on the solubility of perovskite materials which possess more than one soluble cation in their structure.Article Citation - WoS: 7Citation - Scopus: 9Preparation of the Pb(mg1/3nb2 Films by Aqueous Tape Casting(Elsevier Ltd., 2009) Şakar-Deliormanlı, Aylin; Çelik, Erdal; Polat, MehmetLead magnesium niobate (PMN) is a relaxor ferroelectric material. Because of its high dielectric constant and superior electrostrictive properties it is commonly used in the manufacture of multilayer electronic devices which is typically produced by tape casting. However, preparation of PMN slurry formulations to use in aqueous tape casting process is not investigated in detail yet. Therefore, in this study aqueous PMN formulations were developed for tape casting and its relation with the final properties of PMN films were investigated. The slurries were prepared using poly(acrylic acid)-based comb polymer as the dispersant, nonionic acrylic latex as the binder and the hydroxypropyl methyl cellulose as the wetting agent. The results showed that it is possible to prepare flexible, crack-free PMN films using highly concentrated suspensions without using any plasticizer. The study gives guidelines for the aqueous tape casting of PMN and can be adapted to processing of other multi-component metal oxides.Article Citation - WoS: 21Citation - Scopus: 23Adsorption of Anionic Polyelectrolyte and Comb Polymers Onto Lead Magnesium Niobate(Elsevier Ltd., 2008) Şakar-Deliormanlı, Aylin; Çelik, Erdal; Polat, MehmetThis paper presents the results concerning the adsorption mechanism of polyacrylic acid (PAA) and polyacrylic acid/polyethylene oxide (PAA/PEO) comb polymer onto lead magnesium niobate (PMN) powders. In the study adsorption behavior of PAA and PAA/PEO onto PMN surface were determined in aqueous solutions and the influence of pH and ionic strength was investigated. Results showed that adsorption of PAA or PAA/PEO increased with decreasing pH of the suspensions. The increase in the ionic strength or the presence of divalent cations caused an increase in the adsorption of both polyelectrolytes. It was observed that the adsorption reaches a maximum when PAA is fully complexed in solution. On the other hand, the increase in the adsorption of PAA/PEO onto PMN in the presence of monovalent or divalent salt was attributed to the decrease in the electrostatic forces rather than complex formation with the divalent metal ions in solution. Turbidity measurements showed that there is no complex formation between the divalent metal ions and PAA/PEO comb polymers due to shielding effect of the PEO teeth.Article Citation - WoS: 14Citation - Scopus: 18Rheological Behavior of Pmn Gels for Solid Freeform Fabrication(Elsevier Ltd., 2008) Şakar Deliormanlı, Aylin; Çelik, Erdal; Polat, MehmetLead magnesium niobate (PMN) is a relaxor ferroelectric material and have widespread applications in the manufacture of multilayer electronic devices such as ceramic capacitors, actuators and transducers. The dielectric constant of this electrostrictive material is much higher than the well known ferroelectric barium titanate. However, aqueous processing of PMN is not investigated yet especially for the novel wet shaping fabrication. In this study, concentrated aqueous colloidal PMN gels have been designed to use in the robocasting process. Concentrated PMN suspensions were stabilized by polyacrylic acid and then gelation induced by changing the pH or ionic strength of the suspension or by addition of a cationic polyelectrolyte to the system. Through this procedure it was essential to understand the solid-liquid transition under shear to explore the feasibility of forming without excessive use of polymers. Therefore, rheological response of the samples having a gel network was investigated. Results showed that gelation induced by cationic polyethylene imine or by multivalent salts were successful methods in preparation of PMN gels. However, gelation induced by changing the pH of the suspension was challenging due to ion dissolution from PMN surface.Article Citation - WoS: 46Citation - Scopus: 53Preparation and Characterization of Fe2o3-Tio2 Thin Films on Glass Substrate for Photocatalytic Applications(Elsevier Ltd., 2006) Çelik, Erdal; Yıldız, A. Y.; Ak Azem, Necmiye Funda; Tanoğlu, Metin; Toparlı, Mustafa; Emrullahoğlu, Ö. Faruk; Özdemir, İ.Fe2O3-TiO2 coatings were successfully prepared on glass slide substrates using sol-gel method for photocatalytic applications. The phase structure, thermal, microstructure and surface properties of the coatings were extensively characterized by using X-ray diffractometry (XRD), differential thermal analysis/thermograviometry (DTA/TG), scanning electron microscopy (SEM) and atomic force microscopy (AFM). Their adhesion and absorbance properties were investigated by a scratch tester and UV-vis spectroscopy. Four different solutions were prepared by changing Fe/Ti molar ratios. Glass substrates were coated by solutions of Ti-alkoxide, Fe-chloride, glaciel acetic acid and isopropanol. The obtained gel films were dried at 300 °C for 10 min and subsequently heat-treated at 500 °C for 5 min in air. The oxide thin films were annealed at 600 °C for 60 min in air. The influence of Fe3+ concentration and number of layers on structure of the films was established. In addition, XRD results revealed that Fe2O3-TiO2 films composed of TiO2, Fe2Ti3O9, Ti3O5 and Fe3O4 phases. According to DTA/TG result, it was determined that endothermic and exothermic reactions were formed at temperatures between 80 and 650 °C due to solvent removal, combustion of carbon based materials and oxidation of Fe and Ti. SEM observations exhibited that the coating structure becomes more homogeneous depending on an increase of Fe/Ti molar ratios and thus a regular surface morphology forms with increasing Fe/Ti ratio. It was also seen that as the Fe/Ti ratio increases the surface roughness of the films increases. Critical adhesion force of thin films with Fe/Ti ratio of 0, 0.07, 0.18 and 0.73 were found to be 9, 25, 28 and 21 mN, respectively. The methylene blue solutions photocatalyzed by TiO2 based thin films shows characteristic absorption bands at 420 nm.