Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7148
Browse
6 results
Search Results
Article Citation - WoS: 7Citation - Scopus: 7A Comprehensive Study on Burst Pressure Performance of Aluminum Liner for Hydrogen Storage Vessels(ASME, 2021) Kangal, Serkan; Sayı, Abdülmecit Harun; Ayakdaş, Ozan; Kartav, Osman; Aydın, Levent; Artem, Hatice Seçil; Aktaş, Engin; Yücetürk, Kutay; Tanoğlu, Metin; Kandemir, Sinan; Beylergil, BertanThis paper presents a comparative study on the burst pressure performance of aluminum (Al) liner for type-III composite overwrapped pressure vessels (COPVs). In the analysis, the vessels were loaded with increasing internal pressure up to the burst pressure level. In the analytical part of the study, the burst pressure of the cylindrical part was predicted based on the modified von Mises, Tresca, and average shear stress criterion (ASSC). In the numerical analysis, a finite element (FE) model was established in order to predict the behavior of the vessel as a function of increasing internal pressure and determine the final burst. The Al pressure vessels made of Al-6061-T6 alloy with a capacity of 5 L were designed. The manufacturing of the metallic vessels was purchased from a metal forming company. The experimental study was conducted by pressurizing the Al vessels until the burst failure occurred. The radial and axial strain behaviors were monitored at various locations on the vessels during loading. The results obtained through analytical, numerical, and experimental work were compared. The average experimental burst pressure of the vessels was found to be 279 bar. The experimental strain data were compared with the results of the FE analysis. The results indicated that the FE analysis and ASSC-based elastoplastic analytical approaches yielded the best predictions which are within 2.2% of the experimental burst failure values. It was also found that the elastic analysis underestimated the burst failure results; however, it was effective for determining the critical regions over the vessel structure. The strain behavior of the vessels obtained through experimental investigations was well correlated with those predicted through FE analysis.Article Citation - WoS: 23Citation - Scopus: 26Experimental and Statistical Analysis of Carbon Fiber/Epoxy Composites Interleaved With Nylon 6,6 Nonwoven Fabric Interlayers(SAGE Publications Inc., 2020) Beylergil, Bertan; Tanoğlu, Metin; Aktaş, EnginThermoplastic interleaving is a promising technique to improve delamination resistance of laminated composites. In this study, plain-weave carbon fiber/epoxy composites were interleaved with nylon 6,6 nonwoven fabrics with an areal weight density of 17 gsm. The carbon fiber/epoxy composite laminates with/without nylon 6,6 nonwoven fabric interlayers were manufactured by VARTM technique. Double cantilever beam fracture toughness tests were carried out on the prepared composite test specimens in accordance with ASTM 5528 standard. The experimental test data were statistically analyzed by two-parameter Weibull distribution. The results showed that the initiation and propagation fracture toughness Mode-I fracture toughness of carbon fiber/epoxy composites could be improved by about 34 and 156% (corresponding to a reliability level of 0.50) with the incorporation of nylon 6,6 interlayers in the interlaminar region, respectively. The results also revealed that the percent increase in the propagation fracture toughness value was 67 and 41% at reliability levels of 0.90 and 0.95, respectively.Article Citation - WoS: 31Citation - Scopus: 33Modification of Carbon Fibre/Epoxy Composites by Polyvinyl Alcohol (pva) Based Electrospun Nanofibres(Adcotec Ltd., 2016) Beylergil, Bertan; Tanoğlu, Metin; Aktaş, EnginIn this study, the effects of modifying interlaminar region of unidirectional carbon fibre/epoxy composites by the incorporation of electrospun polyvinyl alcohol (PVA) nanofibres were investigated. PVA nanofibres were directly deposited onto the carbon fabrics by electrospinning method to improve mechanical performance of those composites. The features of the electrospun nanofibres were characterized by microscopy techniques. The unidirectional carbon fibre/epoxy composite laminates with/without PVA nanofibre interlayers were manufactured by vacuum-infusion technique in a [0]4 configuration. Tensile, three-point bending, compression, Charpy-impact and Mode-I fracture toughness tests (Double Cantilever Beam (DCB)) were carried out in accordance with ASTM standards to evaluate mechanical performance of the composites. Scanning electron microscopy (SEM) observations were made on the specimens to evaluate microstructural features. It was observed that the carbon fabrics were successfully coated with a thin layer of PVA nanofibres by electrospinning technique. The results showed that P VA nanofibres improve the mechanical properties of unidirectional carbon/epoxy composite laminates when subjected to in-plane loading. On the other hand, PVA nanofibres slightly reduced the mode-I fracture toughness values although they led to more stable crack propagation.Article Citation - WoS: 108Citation - Scopus: 117Enhancement of Interlaminar Fracture Toughness of Carbon Fiber–epoxy Composites Using Polyamide-6,6 Electrospun Nanofibers(John Wiley and Sons Inc., 2017) Beylergil, Bertan; Tanoğlu, Metin; Aktaş, EnginIn this study, carbon fiber–epoxy composites are interleaved with electrospun polyamide-6,6 (PA 66) nanofibers to improve their Mode-I fracture toughness. These nanofibers are directly deposited onto carbon fabrics before composite manufacturing via vacuum infusion. Three-point bending, tensile, compression, interlaminar shear strength, Charpy impact, and double cantilever beam tests are performed on the reference and PA 66 interleaved specimens to evaluate the effects of PA 66 nanofibers on the mechanical properties of composites. To investigate the effect of nanofiber areal weight density (AWD), nanointerlayers with various AWD are prepared by changing the electrospinning duration. It is found that the electrospun PA 66 nanofibers are very effective in improving Mode-I toughness and impact resistance, compressive strength, flexural modulus, and strength of the composites. However, these nanofibers cause a decrease in the tensile strength of the composites. The glass-transition temperature of the composites is not affected by the addition of PA 66 nanofibers. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017, 134, 45244.Article Shear Strength of Pultruded Composite Pins With External Confinement(Taylor and Francis Ltd., 2014) Beylergil, Bertan; Aktaş, Alaattin; Pekbey, YelizWeight reduction using composites has gained increasing attention in recent times. In this study, pultruded composite pins (unconfined and confined) were manufactured and tested by using a custom double shear testing fixture. Different configurations were applied for confinement of the composite pins, including weft-knitted fabrics (plain, 1 × 1 rib, and Milano), woven fabrics and E-glass 130 tex fibers/adhesive cloth. They were externally wrapped and bonded to the unconfined composite pins. In each case, five identical specimens were tested, and shear strength data were analyzed by using two-parameter Weibull statistics. The results showed that the maximum shear strength took its highest value in the unconfined case for both average values of the test results and for 99% reliability under Weibull distribution. The confinement had a negative effect on the average shear strength of the unconfined pins. It was also seen that the 99% reliability values of shear strength were approximately equivalent to the 0.7 average value of the shear strength.Article Citation - WoS: 4Citation - Scopus: 4Enhancement of Flexural Performance of Wood Beams Using Textile Fabrics(Walter De Gruyter Gmbh, 2013) Beylergil, Bertan; Aktaş, Alaattin; Pekbey, YelizThe aim of this study was to investigate the flexural performance of wood beams (beech - Fagus orientalis Lipsky) reinforced with woven and selected weft knitted glass fabrics, namely, Milano and plain knit. Some physical and mechanical properties of the beech wood and the textile fabrics were determined in accordance with relevant ASTM standards. Twenty-four wood beams which have two different cross sections (I-shaped and square hollow) were manufactured and tested under a threepoint load. They were divided into two groups: Group A specimens were not reinforced to serve as a reference, whereas Group B specimens were reinforced with textile fabrics combined with adhesion. The flexural behavior of the specimens was studied through their load-deflection characteristics. The modes of failure were identified and categorized. The experimental results showed that the load-bearing capacity of reinforced beams increased significantly compared to the beam without reinforcement. This method can be used to repair and strengthen damaged wood beams.