Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7148
Browse
2 results
Search Results
Article Citation - WoS: 4Citation - Scopus: 4Formation and Characterisation of Nanoporous Tio2 Layers on Microroughened Titanium Surfaces by Electrochemical Anodisation(Institution of Engineering and Technology, 2014) Dikici, Tuncay; Güzelaydın, Abdurrahman Halis; Toparlı, MustafaNanoporous titanium dioxide (TiO2) layers were successfully formed by an electrochemical anodisation method on microroughened titanium (Ti) surfaces in fluoride containing aqueous electrolyte. Microroughened Ti surfaces were produced by sandblasting with Al2O3 particles of 50 μm in diameter and acid-etching in a blend of HCl/H2SO4 solution. The surface morphology, topography and chemical composition of the specimens were analysed by scanning electron microscopy, atomic force microscopy and X-ray photoelectron spectroscopy. The surface roughness and the wettability of treated Ti surfaces were measured using profilometry and a contact angle measurement system, respectively. With anodising of sandblasted-/acid etched surfaces, micrometre- and nanometre-scale textures on titanium specimens were created. Results showed that these developed nanoporous-microroughened surfaces exhibited lower contact angle values than the other treated Ti surfaces. The sandblasted/acid-etched/anodised Ti specimen had a surface morphology with distinctively formed hills and valleys and higher surface roughness than the other anodised specimens. This study indicated that nanoporous TiO2 structures fabricated on microroughened Ti can be an effective way to modify the titanium surfaces for the future development of implant applications.Article Citation - WoS: 46Citation - Scopus: 53Preparation and Characterization of Fe2o3-Tio2 Thin Films on Glass Substrate for Photocatalytic Applications(Elsevier Ltd., 2006) Çelik, Erdal; Yıldız, A. Y.; Ak Azem, Necmiye Funda; Tanoğlu, Metin; Toparlı, Mustafa; Emrullahoğlu, Ö. Faruk; Özdemir, İ.Fe2O3-TiO2 coatings were successfully prepared on glass slide substrates using sol-gel method for photocatalytic applications. The phase structure, thermal, microstructure and surface properties of the coatings were extensively characterized by using X-ray diffractometry (XRD), differential thermal analysis/thermograviometry (DTA/TG), scanning electron microscopy (SEM) and atomic force microscopy (AFM). Their adhesion and absorbance properties were investigated by a scratch tester and UV-vis spectroscopy. Four different solutions were prepared by changing Fe/Ti molar ratios. Glass substrates were coated by solutions of Ti-alkoxide, Fe-chloride, glaciel acetic acid and isopropanol. The obtained gel films were dried at 300 °C for 10 min and subsequently heat-treated at 500 °C for 5 min in air. The oxide thin films were annealed at 600 °C for 60 min in air. The influence of Fe3+ concentration and number of layers on structure of the films was established. In addition, XRD results revealed that Fe2O3-TiO2 films composed of TiO2, Fe2Ti3O9, Ti3O5 and Fe3O4 phases. According to DTA/TG result, it was determined that endothermic and exothermic reactions were formed at temperatures between 80 and 650 °C due to solvent removal, combustion of carbon based materials and oxidation of Fe and Ti. SEM observations exhibited that the coating structure becomes more homogeneous depending on an increase of Fe/Ti molar ratios and thus a regular surface morphology forms with increasing Fe/Ti ratio. It was also seen that as the Fe/Ti ratio increases the surface roughness of the films increases. Critical adhesion force of thin films with Fe/Ti ratio of 0, 0.07, 0.18 and 0.73 were found to be 9, 25, 28 and 21 mN, respectively. The methylene blue solutions photocatalyzed by TiO2 based thin films shows characteristic absorption bands at 420 nm.