Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7148
Browse
2 results
Search Results
Article Citation - Scopus: 10Development of Lightweight Geopolymer Composites Containing Perlite and Vermiculite(International OCSCO World Press, 2023) Korniejenko, Kinga; Pławecka, Kinga; Bulut, Alperen; Şahin, Baran; Azizağaoğlu, Göksu; Figiela, BeataPurpose: The aim of this work was to prepare and characterise geopolymer composites containing lightweight aggregates-perlite and vermiculite. Design/methodology/approach: The geopolymer matrix was prepared on the basis of fly ash, sand and a 6M sodium hydroxide solution with sodium silicate. The properties of the materials were tested 28 days after the preparation of the samples. The following research methods were used to characterise the composites: compressive and flexural strength tests, microstructural tests using a scanning electron microscope, and thermal conductivity were measured. Findings: The results obtained showed a slight effect of the additives on the strength properties. Lightweight aggregates are characterised by good coherence with the matrix material. Their addition allowed to reduce the density and lowered the thermal conductivity of the materials. The results obtained indicate that the proposed additives can improve the properties of the geopolymer composite for use in the construction industry. Research limitations/implications: Further research should focus on geopolymer composites with perlite and involve fire-resistant and water-absorption tests. Practical implications: The production of lightweight building materials brings a number of benefits, such as reducing the density of building elements and, at the same time, the entire structure, which results in a reduction in their weight, as well as lower transport costs. Such elements have better thermal and acoustic insulation, reflected in the parameters of buildings. An additional advantage is the reduced environmental impact through better insulation properties, lower fuel consumption during transport, etc. Originality/value: The density of the material can be reduced by using lightweight aggregates or obtaining porous material in the foamed process. In the case of geopolymer composites, a number of studies related to foamed materials have been provided, but there is only a few previous research connected with lightweight aggregates such as perlite and vermiculite. © by International OCSCO World Press. All rights reserved. 2023.Article Citation - WoS: 37Citation - Scopus: 41Processing and Characterization of Geopolymer and Sintered Geopolymer Foams of Waste Glass Powders(Elsevier, 2021) Polat, Dilan; Güden, MustafaGeopolymer foams of fine and coarse waste glass (WG) powders were prepared using an activation solution of NaOH (8 M) and Na2SiO3. The effects of WG powder particle size, solid/liquid ratio (S/L = 1, 1.5, and 2) and Al foaming agent content (2-20 wt%) on the expansion and temperature behavior of the slurries were determined in-situ using a laser sensor and a thermocouple, respectively. The geopolymer foams processed using a coarse WG powder slurry, S/L = 2, and 2 wt% Al, were further sintered at 600, 700, 725, and 750 degrees C. The compression strengths and thermal conductivities of the geopolymer and sintered geopolymer foams were also determined. The slurry expansions continued until about a maximum, and the temperatures of the slurries increased to a maximum, 85-88 degrees C. At the maximum temperature, the slurry evaporation and the resultant increase in the S/L ratio limited the slurry expansion. Increasing the Al content decreased the final density of the foams (238-555 kg m-3), while the coarse powder slurries resulted in lower densities than the fine powder slurries. Three crystal phases, muscovite, sodium aluminum silicate hydrate, and thermonitrite, were determined in the geopolymer foams. The muscovite formation was noted to be favored at high S/L ratios. During sintering, the partial melting of glass particles started after about 700 degrees C, while sintering above this temperature decreased the final density of the foams. The reduced density above 700 degrees C was ascribed to the release of CO2 due to the decomposition of thermonitrite. Both the compressive strength and thermal conductivity of the geopolymer and sintered geopolymer foams increased with increasing foam density. The highest increase in the compressive strength and reduction in the density were seen in the geopolymer foams sintered at 750 degrees C.