Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7148
Browse
4 results
Search Results
Article Citation - WoS: 2Citation - Scopus: 2Scanning Probe Oxidation Lithography on Ta Thin Films(American Scientific Publishers, 2008) Okur, Salih; Büyükköse, Serkan; Tarı, SüleymanA Semi-Contact Scanning Probe Lithography Technique (SC-SPL) has been applied to create nano-oxide patterns on Ta thin films grown by DC magnetron sputtering method on SiO 2/Si substrates. The height and linewidth profiles of nano-oxide lines created by a conductive AFM tip on Ta film surfaces were measured as a function of applied voltage, oxidation time, humidity, and tip apex curvature. The AFM surface measurements show that the height of the oxides increases linearly with increasing voltage; but there was no oxide growth, when less than 4 V was applied even at 85% relative humidity. Electrical measurements were performed and the resistivities of the TaO x layer and Ta film were obtained as 5.76 × 10 8 and 1.4 × 10 5 Ohm-cm, respectively.Article Citation - WoS: 12Citation - Scopus: 16Humidity Adsorption Kinetics of a Trypsin Gel Film(Elsevier Ltd., 2012) Okur, Salih; Ceylan, Çağatay; Çulcular, EvrenThis study focuses on the humidity adsorption kinetics of an isopropanol-induced and pH-triggered bovine pancreatic trypsin gel (BPTG). The BPTG was adsorbed on a gold coated Quartz Crystal Microbalance (QCM) substrate with a thickness of 376nm. The morphology of the film was characterized using Atomic Force Microscopy (AFM). QCM was used to investigate the humidity sensing properties of the BPTG film. The response of the humidity sensor was explained using the Langmuir model. The average values of adsorption and desorption rates between 11% RH (relative humidity) and 97% RH were calculated as 2482.5M -1s -1 and 0.02s -1, respectively. The equilibrium constant and average Gibbs Free Energy of humidity adsorption and desorption cycles were obtained as 133,000 and -11.8kJ/mol, respectively. © 2011 Elsevier Inc..Article Citation - WoS: 36Citation - Scopus: 30Humidity Adsorption Kinetics of Calix[4]arene Derivatives Measured Using Qcm Technique(Elsevier Ltd., 2010) Okur, Salih; Kuş, Mahmut; Özel, Faruk; Aybek, Vildan; Yılmaz, MustafaThis study focuses on the characterization of sulphonated calix[4]arene derivative films coated on a quartz substrate with a thickness of 40 nm by spin coating method for humidity detection. The humidity adsorption kinetics of the sulphonated calix[4]arene films was investigated by quartz crystal microbalance (QCM) technique. The Langmuir model was used to determine the adsorption rates and Gibbs free energy for various relative humidities between 11% and 97%. Our reproducible experimental results show that suphonated calix[4]arene films have a great potential for humidity sensing applications at room temperature operations. © 2009 Elsevier B.V. All rights reserved.Article Citation - WoS: 74Humidity Sensing Properties of Zno-Based Fibers by Electrospinning(Elsevier Ltd., 2011) Horzum Polat, Nesrin; Taşçıoğlu, Didem; Okur, Salih; Demir, Mustafa MuammerZinc oxide (ZnO) based fibers with a diameter of 80-100 nm were prepared by electrospinning. Polyvinyl alcohol (PVA) and zinc acetate dihydrate were dissolved in water and the polymer/salt solution was electrospun at 2.5 kV cm-1. The resulting electrospun fibers were subjected to calcination at 500 °C for 2 h to obtain ZnO-based fibers. Humidity sensing properties of the fiber mats were investigated by quartz crystal microbalance (QCM) method and electrical measurements. The adsorption kinetics under constant relative humidity (RH) between 10% and 90% were explained using Langmuir adsorption model. Results of the measurements showed that ZnO-based fibers were found to be promising candidate for humidity sensing applications at room temperature.