Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7148
Browse
3 results
Search Results
Article Citation - WoS: 10Citation - Scopus: 10Effects of Mixture Design Parameters on the Mechanical Behavior of High-Performance Fiber-Reinforced Concretes(American Society of Civil Engineers (ASCE), 2020) Erdem, Tahir Kemal; Erdem, Tahir Kemal; Demirhan, Serhat; Yıldırım, Gürkan; Banyhussan, Qais S.; Şahin, Oğuzhan; Balav, Mohammad H.; Şahmaran, Mustafa; 03.03. Department of Civil Engineering; 03. Faculty of Engineering; 01. Izmir Institute of TechnologyThe main purpose of this research is to assess the influence of different design parameters on the mechanical performance of high-performance fiber-reinforced concrete (HPFRC) mixtures. Special attention is also paid to achieving deflection-hardening behavior in the presence of a large amount of coarse aggregates. Different mixture design parameters were the initial curing ages (3, 7, 28, and 90 days), ratios of Class F fly ash (FA) to portland cement (PC) (0.0, 0.2, and 0.4), addition/type of nanomaterials [nanosilica (NS), nanoalumina (NA), and nanocalcite (NC)], and combinations of fibers [polyvinyl-alcohol + steel (P, S) or brass-coated microsteel + steel (B, S)]. The experimental program included the evaluation of compressive strength, flexural strength, and midspan deflection results in addition to test parameters recorded under biaxial flexural loading via a series of square panel tests, including peak load and energy absorption capacities. Test results revealed that deflection-hardening response coupled with multiple microcracks can be obtained when large amounts of coarse aggregates are available for all HPFRC mixtures. As expected, experimental results change depending on the different curing ages and FA/PC ratios. The most distinctive parameters affecting the results are addition/type of nanomaterials and the presence of different fiber combinations. In the presence of nanomaterials, all results from the different tests improved, especially for NA and NS inclusions. With slight concessions in flexural deflection results, B fiber is shown to be a successful candidate to fully replace costly P fibers because most properties of B, S fiber-reinforced HPFRC mixtures outperformed those with P, S fibers, both under four-point bending and biaxial flexural loading.Article Citation - WoS: 64Citation - Scopus: 78Utilization of Municipal Plastic and Wood Waste in Industrial Manufacturing of Wood Plastic Composites(Springer Verlag, 2020) Başalp, Dildare; Tıhmınlıoğlu, Funda; Sofuoğlu, Aysun; İnal, Fikret; Sofuoğlu, Aysun; Tıhmınlıoğlu, Funda; İnal, Fikret; Sofuoğlu, Sait Cemil; 03.02. Department of Chemical Engineering; 03.07. Department of Environmental Engineering; 03. Faculty of Engineering; 01. Izmir Institute of TechnologyIn this study, Wood Plastic Composites (WPCs) were produced from post-consumer bulky wastes of recycled plastic and wood in order to minimize waste, decrease environmental effects of plastics, reserve natural resources, and support circular economy for sustainable production and consumption. Five different types of polypropylene (PP) or polyethylene (PE) based recycled plastics and wood obtained from urban household bulky wastes were used in the production of recycled WPC composites, r-WPCs. Virgin WPC (v-WPC) and r-WPC compounds were prepared with wood flour (WF) and maleic anhydride grafted compatibilizer (MAPP or MAPE) to evaluate the effect of recycled polymer type and compatibilizer on the mechanical properties. It was found that tensile strength properties of r-WPCs produced from recycled PP (r-PP) were higher than that of the r-WPCs produced from mixed polyolefins and recycled PE. r-WPCs containing anti-oxidants, UV stabilizers, and compatibilizer with different WF compositions were produced from only recycled garden fraction PP (PPFGF) to determine the optimum composition and processing temperature for pilot scale manufacturing of r-WPCs. Based on tensile, impact, flexural, and water sorption properties of r-WPC compounds with different formulations, the optimum conditions of r-WPC compounds for industrial manufacturing process were determined. Surface morphology of fractured surfaces as well as tensile, flexural and density results of r-WPC compounds revealed the enhancement effect of MAPP on interfacial adhesion in r-WPCs. r-WPC products (crates and table/chair legs) based on bulky wastes were produced using an injection molding process at industrial scale by using 30 wt% WF-filled r-WPC compound. This study demonstrated that r-WPC compounds from recycled bulky plastic and wood wastes can be used as a potential raw material in plastic as well as WPC industry, contributing to circular economy. GraphicArticle Citation - WoS: 35Citation - Scopus: 39Development of Graphene Nanoplatelet-Reinforced Az91 Magnesium Alloy by Solidification Processing(Springer Verlag, 2018) Kandemir, Sinan; Kandemir, Sinan; 03.10. Department of Mechanical Engineering; 03. Faculty of Engineering; 01. Izmir Institute of TechnologyIt is a challenging task to effectively incorporate graphene nanoplatelets (GNPs) which have recently emerged as potential reinforcement for strengthening metals into magnesium-based matrices by conventional solidification processes due to their large surface areas and poor wettability. A solidification processing which combines mechanical stirring and ultrasonic dispersion of reinforcements in liquid matrix was employed to develop AZ91 magnesium alloy matrix composites reinforced with 0.25 and 0.5 wt.% GNPs. The microstructural studies conducted with scanning and transmission electron microscopes revealed that fairly uniform distribution and dispersion of GNPs through the matrix were achieved due to effective combination of mechanical and ultrasonic stirring. The GNPs embedded into the magnesium matrix led to significant enhancement in the hardness, tensile strength and ductility of the composites compared to those of unreinforced AZ91 alloy. The strength enhancement was predominantly attributed to the grain refinement by the GNP addition and dislocation generation strengthening due to the coefficient of thermal expansion mismatch between the matrix and reinforcement. The improved ductility was attributed to the refinement of β eutectics by transforming from lamellar to the divorced eutectics due to the GNP additions. In addition, the strengthening efficiency of the composite with 0.25 wt.% GNP was found to be higher than those of the composite with 0.5 wt.% GNP as the agglomeration tendency of GNPs is increased with increasing GNP content. These results were compared with those of the GNP-reinforced magnesium composites reported in the literature, indicating the potential of the process introduced in this study in terms of fabricating light and high-performance metal matrix composites.