    Microstructural Development of Interface Layers Between Co-Sintered Alumina and Spinel Compacts
    (Elsevier Ltd., 2011) Yalamaç, Emre; Carry, Claude; Akkurt, Sedat
    Tests were performed to investigate the microstructure of the interface between alumina and spinel materials after high temperature thermal treatment (1500°C). The first test involved co-sintering of co-pressed alumina and spinel compacts. Microstructures were investigated by SEM, EDS, WDS and EBSD. A microstructurally distinct layer with columnar grains of up to 40μm length and 5μm width was observed after 16h at 1500°C. Growth rate of the columnar spinel grains from parent spinel towards alumina follows parabolic kinetics, controlled by a mixed process of O2- ion diffusion and interface reaction. Diffusion couples of spinel and alumina were investigated. Same columnar spinel grains were observed at the interface which grew into alumina during thermal treatment with the same kinetics as in co-sintering experiments. The shape of the phase boundaries between spinel and alumina can be a further indication of the direction of their growth.
  • Article
    Citation - WoS: 19
    Citation - Scopus: 23
    Silicon Oxycarbide-Based Composites Produced From Pyrolysis of Polysiloxanes With Active Ti Filler
    (Elsevier Ltd., 2006) Akkaş, Hatice Deniz; Öveçoğlu, M. Lütfi; Tanoğlu, Metin
    Phenyl (PPS) and methyl (PMS) containing polysiloxanes were pyrolyzed at elevated temperatures (900-1500 °C) under argon atmosphere to investigate the phase developments within the polymers. It was found that pyrolysis of the polymers under inert atmosphere up to 1300 °C leads to amorphous silicon oxycarbide (SiOxCy) ceramics. Conversions at higher temperatures results in the transformations into the crystalline β-SiC phases. Ceramic matrix composites (CMCs) were developed based on the active filler controlled pyrolysis (AFCOP) of polysiloxanes with active Ti filler additions. CMC monoliths were prepared with 60-80 wt.% of active Ti particulates blended into polymer precursors. Green bodies of the composites were made by warm pressing under 15 MPa pressure and ceramics were obtained by pyrolysis at elevated temperatures between 900 and 1500 °C under argon atmosphere. The results showed that due to the incorporation of active Ti fillers, formation of crystalline phases such as TiC, TiSi, and TiO occured within the amorphous matrix due to the reactions between the Ti and the polymer decomposition products. The microstructural and mechanical characterization results of the composites are presented within the paper.