Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7148
Browse
3 results
Search Results
Article Citation - WoS: 1Citation - Scopus: 1Fast Firing Technique for Martian Regolith Simulant: Advancing Isru Capabilities(Academic Press inc Elsevier Science, 2025) Karacasulu, Levent; Tomasini, Alessandro; Vakifahmetoglu, Cekdar; Biesuz, MattiaIn-Situ Resource Utilization (ISRU) approaches hold significant importance in plans for space colonization. This work explores a different ISRU concept applying fast-firing, a robust and well-known industrial process, to Mars regolith simulant (MGS-1). The fast-fired specimens were compared to the ones obtained by conventional sintered under low heating rates. When the holding time at the firing temperature is longer than 15 min, fast-fired specimens exhibited higher density and flexural strength (> 35 MPa) than conventional sintering. For both processes, the bulk density values and the mechanical properties of the regolith compacts were enhanced with increasing dwell time. This was attributed to higher heating rates changing the densification/crystallization kinetics involving the basalt glass in the regolith composition. Specifically, high heating rate promotes sintering over crystallization. On these bases, fast firing can be considered a potential candidate for ISRU on Mars.Article Citation - WoS: 3Citation - Scopus: 3Effects of Different Precursors on the Aging and Electrocaloric Properties of Mn-Doped Ba0.95sr0.05tio3 Ceramics(Springer, 2023) Karakaya, Merve; Erdem, Emre; Akdoğan, Yaşar; Adem, UmutIn this study, the effects of different types of Mn precursors (MnO2 and Mn2O3) and sintering temperature on the defect dipole formation, ferroelectric aging and electrical properties were investigated by using Ba0.95Sr0.05TiO3 ceramics as the base. Both Mn precursors were substituted to the Ti-site as 1 mol% and two different sintering temperatures of 1325 and 1400 degrees C were used to study the effect of grain size. We deduced that slightly higher amounts of Mn2+ can be incorporated into the perovskite structure when MnO2 is used as the precursor, by using X-ray diffraction and electron paramagnetic resonance spectroscopy. Mn-doped samples sintered at 1325 degrees C age faster than those sintered at 1400 degrees C. Aging caused a decrease in the electrocaloric effect whereas Mn-doping increased it. This study shows that Mn precursor used for the acceptor doping affects the amount of Mn incorporated into the structure and therefore electrical properties of the resulting ceramics.Article Citation - WoS: 19Citation - Scopus: 17Preparation and Characterization of Nanocrystalline Titania Powders by Sonochemical Synthesis(Elsevier Ltd., 2012) Çağlar Duvarcı, Özlem; Çiftçioğlu, MuhsinNanocrystalline mesoporous titania powders were synthesized by hydrolyzing titanium isopropoxide in ethanol-water mixtures which were ultrasonically treated without using any templates or chemicals. Titanium isopropoxide-ethanol mixture was added dropwise to a water-ethanol mixture placed in an ultrasonic bath. The properties of the sonochemically synthesized powder were compared with those of the powders prepared without ultrasonic treatment along with Degussa P-25 titania powder. The phase structure, crystallite size, surface area, particle size, powder density were determined and sintering behavior was analyzed in this work. The nanotitania powder prepared during ultrasonic induced hydrolysis (TiO 2-U) was determined to be formed from a mixture of anatase and brookite phases at 25°C. The brookite phase in nanotitania powder prepared without ultrasonic treatment (TiO 2-NoU) was detected at 70°C. The anatase-rutile phase transformation was completed in the 500-700°C range for both powders. The average crystallite sizes of the powders at 25°C were determined as 10 and 5nm for TiO 2-NoU and TiO 2-U, respectively. The surface area decreased from 238 to106m 2/g for TiO 2-NoU and from 287 to 82m 2/g for TiO 2-U when the calcination temperature was increased from 200 to 500°C. The evolution of the N 2 adsorption-desorption behavior with calcination temperature and the corresponding pore size distributions/volumes was attributed to the formation of closely packed submicron aggregates during powder synthesis and calcination. The sintering behavior was concluded to be controlled by 7-10nm crystallites and the submicron aggregates. The determination of the densification behavior of titania powders prepared by different methods with various levels of dopants may prove to be very useful for a better understanding of the phase/pore structure evolution which is crucial for a significant number of applications.