Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7148
Browse
5 results
Search Results
Now showing 1 - 5 of 5
Article Citation - WoS: 15Citation - Scopus: 15The Effect of Strain Rate on the Compression Behavior of Additively Manufactured Short Carbon Fiber-Reinforced Polyamide Composites With Different Layer Heights, Infill Patterns, and Built Angles(Springer, 2023) Zeybek, Mehmet Kaan; Güden, Mustafa; Taşdemirci, AlperPrevious studies on the fused deposition modelling (FDM) processed short carbon fiber/Polyamide 6 (PA6) matrix composites and neat PA6 have mostly concentrated on the quasi-static mechanical properties. Present study focused on the strain rate-dependent deformation behavior of a short carbon fiber-reinforced PA6 (Onyx) and neat PA6, produced in different layer heights, infill patterns and built angles. As compared with PA6, Onyx showed a higher compression stress at all strain rates investigated. A layer height of 0.2 mm in PA6 specimens promoted a better bonding between [0/90°] infill layers; hence, a higher flow stress than 0.2 mm layer height specimens, while 0.2 mm layer height induced a higher porosity in Onyx specimens, leading to a lower flow stress. The porosities in Onyx [0/90°] infill specimens were due to the constraining effect of 0/90° fiber layers. Changing infill pattern from a [0/90°] to a concentric one decreased porosity at the same layer height and hence increased the compressive flow stress. The highest compressive strength was found in the specimens with the loading axis 90 and 0° to [0/90°] infill plane. The lowest strength was, however, determined in the specimens with the loading axis 30 and 60o to [0/90°] infill plane in quasi-static loading. However, the specimens with the loading axis of 60, 45, 30 and 0° exhibited a brittle behavior in high strain rate loading (1500 s−1). The specimens with the loading axis of 45° had the lowest fracture stress and strain in the high strain rate loading. This signified the importance of loading angle at high strain rates. Finally, the rate sensitivities of PA6 and Onyx specimens were shown to be similar, showing a matrix dominated deformation. However, the strain rate jump tests indicated a slightly higher rate sensitivity of Onyx specimens at quasi-static strain rates (10−3-10−1 s−1).Article Citation - WoS: 39Citation - Scopus: 40Impact Loading of Functionally Graded Metal Syntactic Foams(Elsevier, 2022) Movahedi, Nima; Fiedler, Thomas; Taşdemirci, Alper; Murch, Graeme E.; Belova, Irina V.; Güden, MustafaThe present study addresses the impact loading of functionally graded metal syntactic foams (FG-MSF). For comparison, samples of the same material were also compression loaded at quasi-static velocities. Samples of A356 aluminium FG-MSF were produced using counter-gravity infiltration casting with combination of equal-sized layers of expanded perlite (EP) and activated carbon (AC) particles. A modified Split Hopkinson Pressure Bar test set-up was used to impact the FG-MSFs from their EP or AC layers at 55 m/s or 175 m/s impact velocities. A high-speed camera captured the deformation of the samples during testing. It was shown that increasing the loading velocity enhanced both the compressive proof strength and energy absorption of the impacted FG-MSF from both layers, confirming a dynamic strengthening effect of the foam. The samples impacted from both layers at 55 and 175 m/s showed a transition and a shock mode of deformation, respectively. The impacted samples at 55 m/s experienced lower final average strain values compared to 175 m/s.Article Citation - WoS: 28Citation - Scopus: 34The Strain Rate Sensitive Flow Stresses and Constitutive Equations of a Selective-Laser and an Annealed-Rolled 316l Stainless Steel: a Comparative Study(Elsevier, 2022) Güden, Mustafa; Enser, Samed; Bayhan, Mesut; Taşdemirci, Alper; Yavaş, HakanThe strain rate dependent compressive flow stresses of a Selective-Laser-Melt 316L (SLM-316L) alloy and a commercial (annealed-extruded) 316L (C-316L) alloy were determined, for comparison, between 1x10-4 and ∼2500 s-1 and between 1x10-4 and ∼2800 s-1, respectively. The Johnson and Cook flow stress material model parameters of both alloys were also determined. The microstructural examinations of the deformed cross-sections of tested specimens (interrupted tests) showed a twinning-induced-plasticity in SLM-316L alloy and a martensitic transformation-induced-plasticity in C-316L alloy. Twin and martensite formations were detected microscopically higher in the dynamically tested specimens until about 0.22 strain, while the twin and martensite formations decreased at increasing strains due to adiabatic heating. The rate sensitivity of SLM-316L was determined slightly higher than that of C-316L within the quasi-static strain rate range (1x10-4 and 1x10-2 s-1), while the rate sensitivities of both alloys were similar in the quasi-static-high strain rate range (1x10-4 and ∼2500-2800 s-1) at low strains. A more rapid decrease in the rate sensitivity of C-316L at increasing strains was found in the quasi-static-high strain rate range. The similar activation volumes of both alloys, corresponding to the dislocation intersections, indicated a similar thermally activated deformation process involvement in both alloys.Article Citation - WoS: 13Citation - Scopus: 14The Quasi-Static Crush Response of Electron-Beam Ti6al4v Body-Centred Lattices: The Effect of the Number of Cells, Strut Diameter and Face Sheet(Wiley, 2022) Güden, Mustafa; Alpkaya, Alican Tuncay; Arslan Hamat, Burcu; Hızlı, Burak; Taşdemirci, Alper; Tanrıkulu, A. Alptuğ; Yavaş, HakanThe effect of the number of cells, strut diameter and face sheet on the compression of electron-beam-melt (EBM) Ti6Al4V (Ti64) body-centred-cubic (BCC) lattices was investigated experimentally and numerically. The lattices with the same relative density (~0.182) were fabricated with and without 2-mm-thick face sheets in 10 and 5 mm cell size, 8–125 unit cell (two to five cells/edge) and 2 and 1 mm strut diameter. The experimental compression tests were further numerically simulated in the LS-DYNA. Experimentally two bending-dominated crushing modes, namely, lateral and diagonal layer crushing, were determined. The numerical models however exhibited merely a bending-dominated lateral layer crushing mode when the erosion strain was 0.4 and without face-sheet models showed a diagonal layer crushing mode when the erosion strain was 0.3. Lower erosion strains promoted a diagonal layer crushing mode by introducing geometrical inhomogeneity to the lattice, leading to strain localisation as similar to the face sheets which introduced extensive strut bending in the layers adjacent to the face sheets. The face-sheet model showed a higher but decreasing collapse strength at an increasing number of cells, just as opposite to the without face-sheet model, and the collapse strength of both models converged when the number of cells was higher than five-cell/edge. The decrease/increase of the collapse strengths of lattices before the critical number of cells was claimed mainly due to the size-imposed lattice boundary condition, rather than the specimen volume. The difference in the experimental collapse strengths between the 5- and the 10-mm cell-size lattices was ascribed to the variations in the microstructures—hence the material model parameters between the small-diameter and the large-diameter EBM-Ti64 strut lattices.Article Citation - WoS: 10Citation - Scopus: 12Testing and Modeling Blast Loading of a Sandwich Structure Cored With a Bio-Inspired (balanus) Core(Elsevier, 2022) Tüzgel, Fırat; Akbulut, Emine Fulya; Güzel, Erkan; Yücesoy, Atacan; Şahin, Selim; Taşdemirci, Alper; Güden, MustafaThe blast loading response of a sandwich structure consisted of bio-inspired (balanus) cores/units was investigated experimentally and numerically. A Direct Pressure Pulse (DPP) set-up was used to impose a blast-like loading. The equivalent blast conditions corresponding to the used impact velocities were implemented in the models. A benchmark study was performed by using three different methods namely pure Lagrangian, Arbitrary Lagrangian Eulerian, and hybrid. Dynamic crushing behavior was analyzed and exhibited a higher specific energy absorption capacity than its constituents (core and shell). Among the core configurations, all-front configuration was found the most efficient configuration regarding the specific energy absorption.