Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7148
Browse
3 results
Search Results
Now showing 1 - 3 of 3
Article Citation - WoS: 2Citation - Scopus: 1Pressureless Synthesis and Consolidation of the Entropy-Stabilized (hf<sub>0.25</Sub>zr<sub>0.25< Composite by Ultra-Fast High-Temperature Sintering (uhs)(Elsevier Sci Ltd, 2025) Feltrin, Ana C.; De Bona, Emanuele; Karacasulu, Levent; Biesuz, Mattia; Sglavo, Vincenzo M.; Akhtar, FaridEntropy-stabilized Ultra High-Temperature Ceramics (UHTC) offer a groundbreaking solution to the challenges of extreme environments, showcasing enhanced mechanical properties, thermal stability, and resistance to oxidation at high temperatures. The consolidation of UHTC by ultra-fast high-temperature sintering (UHS) significantly reduces processing times and temperature and can produce dense high-performance ceramics with superior mechanical properties. This study reports the pressureless synthesis and consolidation of the entropy-stabilized (Hf0.25Zr0.25Ti0.25V0.25)B-2-B4C composite through UHS within 1 minute, starting from transition metal diboride powders. B4C acts as an effective sintering aid, promoting the densification of the system and the formation of a nearly single-phase hexagonal diboride with a diboride-eutectic phase. Furthermore, a secondary minor hexagonal phase rich in V and Zr is formed close to the eutectic regions. Sintering currents of 40 A were necessary to reach densities higher than 90 % under pressureless conditions, achieving nano hardness higher than 27.3 GPa, comparable with high-entropy diborides produced by Spark Plasma Sintering. The study highlights the entropy-stabilized phase formation, diffusion, densification, and grain growth mechanisms involved during UHS. The work contributes to the understanding of entropy-stabilized ceramics produced by UHS as a faster and less energy-consuming process than conventional sintering methods.Article Citation - WoS: 1Citation - Scopus: 1Pressureless Joining of Soda Lime Silicate Glass Using Polysilazane-Derived Silica at Near-Room Temperature(Elsevier Sci Ltd, 2025) Karacasulu, Levent; Biesuz, Mattia; Pastorelli, Virginia; Vakifahmetoglu, Cekdar; Sglavo, Vincenzo M.; Ferraris, Monica; Soraru, Gian D.Perhydropolysilazane (PHPS) pre-ceramic polymer was used to join soda lime silicate glass at temperatures below 200 degrees C under pressureless conditions. The results show that: (i) the junction material is largely converted to silica at 100 degrees C and fully converted to glass at 150 degrees C; (ii) the samples treated at room temperature and 100 degrees C show a perfectly dense and clean bond, whereas porosity develops starting from 150 degrees C as a result of the hydrolysis reactions and solvent evaporation; (iii) a maximum tensile bond strength of about 5-6 MPa is obtained after treatments at 100 degrees C. Remarkably, after treatment at 500 degrees C, the junction remains intact. These preliminary findings provide the first successful attempt regarding the use of PHPS as a joining material to produce inorganic and transparent bonds for glass at relatively low temperatures.Article Citation - WoS: 23Citation - Scopus: 23Cold Sintering of Soda-Lime Glass(Elsevier Ltd., 2021) Karacasulu, Levent; Ögür, Ezgi; Pişkin, Cerem; Vakıfahmetoğlu, ÇekdarOrdinary recycled soda lime glass powder was densified via cold sintering process with the aid of concentrated NaOH solution. Increase in processing time, temperature and concentration of the NaOH solution resulted in the formation of monolithic glass artifacts with higher relative densities. The sample densified the most (95.2%) was obtained when the sintering was performed at 250˚C with a 20 min dwell time using 15 M NaOH solution.