Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7148
Browse
3 results
Search Results
Now showing 1 - 3 of 3
Article Citation - WoS: 1Citation - Scopus: 1Chemical Composition Optimization and Isothermal Transformation of Δ-Transformation Plasticity Steel for the Third-Generation Advanced High-Strength Steel Grade(Wiley-v C H verlag Gmbh, 2024) Okur, Onur; Davut, Kemal; Palumbo, Gianfranco; Nalcaci, Burak; Guglielmi, Pasquale; Yalcin, Mustafa Alp; Erdogan, MehmetA new low-manganese transformation-induced plasticity steel is designed with optimized nickel content to achieve superior strength and ductility while minimizing the use of expensive nickel. The steel is optimized using JMatPro software, then cast, and hot rolled. To assess the effect of intercritical annealing on austenite (martensite at room temperature) volume fraction and carbon content, hot-rolled steel samples quenched from different annealing temperatures (680-1100 degrees C) are used. Additionally, hot-rolled steel coupons are intercritically annealed at about 50% austenite formation temperature (740 degrees C) and then subjected to isothermal treatments at 300-425 degrees C for varying times (10-90 min). After optimizing these treatments to maximize retained austenite (RA), tensile specimens are heat-treated first at 740 degrees C and then isothermally at 325 degrees C. Thermodynamic calculations suggest that aluminum combined with silicon may lead to the delta ferrite formation, and even minimal nickel content can stabilize a considerable amount of austenite. In the experimental studies, it is shown that lower-temperature bainitic holding enhances austenite stability by enriching the carbon content. Optimized two-stage heat treatments yield up to 25.8% RA, with a tensile strength of 867.2 MPa and elongation of 40.6%, achieving a strength-elongation product of 35.2 GPax%, surpassing the third-generation advanced high-strength steel grades minimum requirement of 30 GPax%.Article Citation - WoS: 5Citation - Scopus: 6Effect of Coiling Temperature on the Structure and Properties of Thermo-Mechanically Rolled S700mc Steel(Technical Faculty in Bor, 2022) Di Nunzio, P. E.; Cesile, M. C.; Oktay, S.; Davut, Kemal; Şeşen, M. K.The boron-free S700MC steel is usually produced by exploiting the properties of a ferrite-bainite mixed microstructure formed by coiling the strips at a temperature of about 450 degrees C, i.e.below the bainite starting temperature. With the aim of further enhancing the mechanical properties of 6 to 10 mm thick strips, industrial tests were carried out at a coiling temperature of 600 degrees C to promote the formation of a structure of ferrite and carbides, which is also acceptable for this type of steel. Unexpectedly, a microstructure composed of ferrite and martensite was obtained. Compared to the ferritic-bainitic grade, the new structure is characterized by a slight decrease of the yield point but by an increase of the ultimate tensile strength by no less than 80 MPa, with a transition from a quasi-discontinuous to a clearly continuous yielding behaviour. Accordingly, the ratio of yield strength to tensile strength decreases from 0.90 to 0.75 and the impact energy decreases by 35 J and 60 J for the two gauge levels, respectively. The mechanical behaviour of the strips coiled at high temperature is explained as a direct consequence of the dual phase structure with a hard phase interspersed in a soft ferrite matrix. The presence of martensite is explained by the so-called incomplete bainite reaction. The partial transformation into ferrite after coiling and the long time required for the coil to cool down stabilize the untransformed austenite due to the carbon enrichment making bainite formation at lower temperatures impossible.Article Citation - WoS: 3Citation - Scopus: 4Partial Austenitisation and Tbf Steel Composed of Ferrite, Bainitic Ferrite, and Austenite(Taylor & Francis, 2022) Erişir, Ersoy; Bilir, Oğuz Gürkan; Sözer, Yunus Emre; Ararat, Özge; Davut, KemalA TRIP-aided bainitic-ferritic (TBF) steel with a chemical composition of Fe-0.19C-1.7Mn-1.09Si-0.51Al-0.05Nb (wt-%) was partially austenitised from a hot-rolled martensitic initial microstructure. After the hot rolling, the martensitic specimens were reheated to different intercritical temperatures and then austempered at 350 degrees C. Thus, the effect of the initial microstructure of TBF steel on intercritical austenite formation during partial austenitisation was studied. The microstructures were investigated by scanning electron microscopy and electron backscatter diffraction (EBSD), and the tensile properties were tested. Microstructural observations revealed that a final microstructure of fine ferrite, bainitic ferrite, and retained austenite can be obtained. The steel partial austenitised at 770 degrees C showed a good combination of ultimate tensile strength and total elongation.