  • Article
    Citation - WoS: 4
    Citation - Scopus: 5
    The Effect of Geometrical Characteristics of Tio2 Nanotube Arrays on the Photocatalytic Degradation of Organic Pollutants
    (Springer, 2023) Kartal, Uğur; Uzunbayır, Begüm; Doluel, Eyyüp Can; Yurddaşkal, Metin; Erol, Mustafa
    Highly ordered TiO2 nanotube arrays (TNAs) were fabricated by electrochemical anodization under varying durations and voltages. The effects of the anodizing parameters on geometrical properties were investigated. The results showed that as the anodizing time increased from 15 to 45 min, the length of the nanotubes increased, but there was no change in their diameter, hence the surface area increased while the open porosity did not change. When the effect of the anodizing voltage was examined, it was observed that both the length and diameter increased as the voltage increased from 15 to 45 V. Thus, a significant increase in open porosity and surface area was observed. The UV-Vis spectrophotometer was used to evaluate the effects of all geometrical characteristics on the photodegradation of methylene blue (MB). The results showed that the anodizing parameters were highly effective on the photocatalytic degradation of MB. With the decrease of the anodizing voltage, the photocatalytic activity increased because of the geometrical characteristics of TNAs. Accordingly, TNAs with the surface area of 25 m(2)/g and the open porosity of 35% obtained by anodizing for 45 min at 15 V showed the highest photocatalytic activity with a degradation efficiency of similar to 81% in 7 h.
  • Article
    Citation - WoS: 9
    Citation - Scopus: 9
    Zno Nanostructures for Photocatalytic Degradation of Methylene Blue: Effect of Different Anodization Parameters
    (Springer, 2022) Öksüz, Ahmet Emrecan; Yurddaşkal, Metin; Kartal, Uğur; Dikici, Tuncay; Erol, Mustafa
    In this paper, the photocatalytic activity of ZnO nanostructures formed by anodization method with different parameters was investigated. The synthesis of ZnO nanostructures with different morphology by varying anodic oxidation parameters containing electrolytes, molarity, voltage, and duration was analyzed. ZnO nanostructures were prepared through different parameters consisting of six samples. The produced ZnO nanostructures were investigated by using X-ray diffraction, scanning electron microscopy, diffuse reflectance spectroscopy, and UV-Vis spectrophotometer. It was found that the morphology of ZnO structures was formed as nanorods, needle-like, flower-like, heterogeneous, and homogeneous of mixed structures. ZnO nanostructures were identified by matching X-Ray diffraction peaks due to the international center for diffraction data database. Experiments on photocatalytic degradation of methylene blue demonstrated that the photocatalytic activity of ZnO samples. The best photocatalytic performance was observed by the sample anodized for an hour in 0.05 M of KHCO3 electrolytes with 40 V electrical potential. It was observed that the removal of methylene blue increased 3 times (photocatalytic degradation efficiency similar to 31% for methylene blue vs similar to 90% by the best sample) thanks to the obtained ZnO nanostructured photocatalysts. The results showed that an increment of the voltage has a significant effect on the photocatalytic activity of ZnO while keeping other parameters including molarity, time, and electrolyte type constant.
  • Article
    Citation - WoS: 8
    Citation - Scopus: 7
    A Comparative Study on Structural, Morphological and Photocatalytic Properties of Anodically Grown Zno Nanowires Under Varying Parameters
    (Springer, 2021) Özdemir, Erdem Tevfik; Kartal, Uğur; Dikici, Tuncay; Erol, Mustafa; Yurddaskal, Metin
    In this study, zinc oxide (ZnO) nanowires (NWs) were successfully produced on Zn plates through electrochemical anodization in potassium bicarbonate aqueous electrolytes with different production parameters in two groups as applied voltage and anodization time. Subsequently, the ZnO NWs were annealed at 300 degrees C for 1 h in air atmosphere to increase crystallinity and remove organic residues. Structural and morphological properties were determined through X-ray diffraction (XRD) and scanning electron microscopy (SEM) analysis. The effect of anodization parameters on the structure of ZnO NWs and thus their photocatalytic activities were evaluated in detail by UV spectrophotometer. The results pointed out that, the most effective nanostructure on the photocatalytic degradation of methylene blue was obtained in the sample that was anodized for 30 min under 30 V at room temperature with a degradation efficiency of 90.6% after 11 h. This result shows that the NW-structured ZnO materials are promising to be used as effective photocatalysts in the removal of organic pollutants by solar energy and their conversion to green compounds.