Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7148
Browse
2 results
Search Results
Now showing 1 - 2 of 2
Article Citation - WoS: 8Citation - Scopus: 8Reducing the Efficiency Roll Off and Applied Potential-Induced Color Shifts in Cdse@zns/Zns-based Light-Emitting Diodes(American Chemical Society, 2020) Özgüler, Şahika; Diker, Halide; Ünlütürk, Seçil Sevim; Özçelik, Serdar; Varlıklı, CananGreen light-emitting CdSe@ZnS/ZnS (QD) nano-particles were synthesized; the photophysical and morphological properties of their films, which were prepared by spin coating from six different concentrations, corresponding to absorbance values of 0.6, 1.1, 1.6, 2.1, 2.8, and 4.0, were determined. Increasing the absorbance value from 0.6 to 4.0 did not change the photophysical properties of QD films to a large extent, whereas it resulted in an increment in QD film thickness from 20 to 110 nm. The films were utilized as an emissive layer in QD light-emitting diodes with poly(9-vinylcarbazole) (PVK), PVK:2-(4-biphenyllyl)-5-(4-tert-butylphenyl)-1,3,4-oxadiazole (PBD), and PVK:1,3-bis[(4-tert-butylphenyl)-1,3,4-oxadiazolyl]-phenylene (OXD-7) hole-transport layers (HTLs). The presence of PBD or OXD-7 in PVK reduced the efficiency values but played a positive role in the color purity and efficiency roll off. The maximum color temperature and electroluminescence wavelength shifts obtained with applied potential were 109, 50, and 50 K and 11, 5, and 5 nm for pure-PVK, PVK:PBD, and PVK:OXD-7-based devices, respectively. Hole mobility, capacitance (at 10(3) Hz), and charge-transfer efficiency values were 9.0 x 10(-7), 6.8 x 10(-7), and 4.2 x 10(-7) cm(2) V s(-1), 1.7, 1, and 1 nF, and 6.90%, 15.50%, and 16.10% for pure-PVK, PVK:PBD, and PVK:OXD-7-based devices, respectively. Enhanced color purity and lowered efficiency roll off obtained with PVK:PBD and PVK:OXD-7 HTLs were attributed to decreased capacitance, increased charge-transfer efficiency, and reduced Joule heating.Article Citation - WoS: 5Citation - Scopus: 6Contribution of O-2 Plasma Treatment and Amine Modified Gos on Film Properties of Conductive Pedot:pss: Application in Indium Tin Oxide Free Solution Processed Blue Oled(Elsevier, 2019) Diker, Halide; Yeşil, Fatih; Varlıklı, CananPrimary (n-propyl amine, n-PRYLA), secondary (dipropyl amine, DPRYLA) and alcohol (propanol amine, PRPOHA) amine derivatives were used as amine sources in graphene oxide (GO) modification and obtained samples were named as nPRYLA-GO, DPRYLA-GO and PRPOHA-GO, respectively. Modified graphene oxide (mGO) derivatives were doped in poly (3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PH1000) and O-2 plasma treatment (70W, 3 min) was applied on the spin casted films. PH1000:mGO films presented high optical transparency values (> 90%) and low resistivity (177-183 Q/sq). The roughness values were increased especially when the hydrophobic alkyl chain containing DPRYLA-GO and nPRYLA-GO were doped in PH1000. Prepared films were utilized as anode in solution processed blue organic light emitting diode. PH1000:PRPOHA-GO anode presented more than 30 nm of decrement in full with at half maximum and 1.6, 1.5 and 1.9 fold enhancements in current, power and external quantum efficiency values, compared to those of ITO anode, respectively.