  • Article
    Citation - WoS: 14
    Citation - Scopus: 14
    Dispersion Stability of Amine Modified Graphene Oxides and Their Utilization in Solution Processed Blue Oled
    (Elsevier Ltd., 2020) Diker, Halide; Bozkurt, Hakan; Varlıklı, Canan
    Graphene oxide (GO) was modified with amine derivatives which contain short (SACA) and long (LACA) alkyl chains. SACAs were n-propylamine, dipropylamine, propanolamine and LACAs were 2-ethylhexylamine, di-hexylamine, dioctylamine, and 1,12-diaminododecane and modified GOs (mGOs) were named as nPRYLA-GO, DPRYLA-GO, PRPOHA-GO, 2EHA-GO, DHA-GO, DOA-GO, and DADOD-GO, respectively. Amine modification resulted in approximately 2-folds of decrement in d-spacing of GO (8.36 angstrom). The C:O ratio, N% and d-spacing values were increased as the alkyl chain length of amine source increased. Except for PRPOHA-GO, all of the mGOs were thermally stable until 100 degrees C. All mGOs were dispersed in dimethylformamide (DMF), ethylene glycol (EG) and isopropyl alcohol (iPA). Regardless of their structural differences, all of the mGOs formed stable dispersions in DMF, whereas SACA-mGOs and LACA-mGOs were compatible with EG and iPA, respectively. DMF, EG and iPA dispersions of DOA-GO, 2EHA-GO, nPRYLA-GO and PRPOHA-GO were doped in Al4083 and prepared composites were utilized as hole transport layer in solution processed blue OLEDs. Ground state energy levels of Al4083:DOA-GO, Al4083:EG, Al4083:PRPOHA-GO, Al4083:2EHA-GO and Al4083:nPRYLA-GO extracted from their X-ray photoelectron spectra were 0.49 eV, 0.67 eV, 0.91 eV, 0.98 eV and 1.00 eV below the work function of ITO, respectively. Among all Al4083:mGOs, the best device performance was obtained with the device that contains Al4083:DOA-GO (in EG), which presented 1.6, 1.7 and 1.5 fold enhancements in current, power and external quantum efficiencies, respectively, compared to those of Al4083:EG based device.
  • Article
    Citation - WoS: 5
    Citation - Scopus: 6
    Contribution of O-2 Plasma Treatment and Amine Modified Gos on Film Properties of Conductive Pedot:pss: Application in Indium Tin Oxide Free Solution Processed Blue Oled
    (Elsevier, 2019) Diker, Halide; Yeşil, Fatih; Varlıklı, Canan
    Primary (n-propyl amine, n-PRYLA), secondary (dipropyl amine, DPRYLA) and alcohol (propanol amine, PRPOHA) amine derivatives were used as amine sources in graphene oxide (GO) modification and obtained samples were named as nPRYLA-GO, DPRYLA-GO and PRPOHA-GO, respectively. Modified graphene oxide (mGO) derivatives were doped in poly (3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PH1000) and O-2 plasma treatment (70W, 3 min) was applied on the spin casted films. PH1000:mGO films presented high optical transparency values (> 90%) and low resistivity (177-183 Q/sq). The roughness values were increased especially when the hydrophobic alkyl chain containing DPRYLA-GO and nPRYLA-GO were doped in PH1000. Prepared films were utilized as anode in solution processed blue organic light emitting diode. PH1000:PRPOHA-GO anode presented more than 30 nm of decrement in full with at half maximum and 1.6, 1.5 and 1.9 fold enhancements in current, power and external quantum efficiency values, compared to those of ITO anode, respectively.