Master Degree / Yüksek Lisans Tezleri
Permanent URI for this collectionhttps://hdl.handle.net/11147/3008
Browse
2 results
Search Results
Master Thesis Development of Keratin Based Hydrogel Systems(Izmir Institute of Technology, 2022) Yalçın Göl, Damla; Top, AybenIn this study, keratin proteins from Merino sheep wool were obtained via oxidative extraction (Chapter 2), sulfitolysis extraction (Chapter 3) and sulfitolysis with reductive extraction methods (Chapter 4). Keratin proteins were characterized XRD and FTIR spectroscopy and thermal analysis. In the SDS-PAGE gel results of the keratins diffusive protein bands between ~23 kDa and >170 kDa and a discrete band at about 12 kDa were observed confirming highly polydisperse nature of the protein samples. Then, keratin-based hydrogel systems were obtained via different methodologies. In Chapter 2, oxidized keratins (keratoses) were crosslinked with THPC to form keratose hydrogels. Effect of the amount of the crosslinking agent on the viscoelastic, swelling, and morphological properties of hydrogels was investigated. In Chapter 3, the keratin hydrogels were obtained via reformation of disulfide bridge and self-assembly of the keratin chains. In Chapter 4, keratins reduced with DTT were crosslinked with 2000 Da PEG-(C2H4-mal)2 and 6000 Da PEG-(C2H4-mal)2 to prepare PEG-hydrogels. Storage moduli of the hydrogels were obtained in the range of 63 ± 22 and 2613 ± 254 Pa and were shown to be tuned by the amount and chain length of the crosslinker. The highest swelling ratios were obtained for the THPC crosslinked hydrogels whereas the highest pore size was observed in PEG-keratin hydrogels. Cytocompatibility of the keratin based hydrogel systems was confirmed using L929 mouse fibroblast cells by applying CCK-8 tests. Of these hydrogels, PEG-keratin hydrogels were found to support cell proliferation with a higher rate than empty TCPS wells up to 4 days. These results demonstrate that low-cost keratin-based hydrogels can be used in a variety of biomedical applications, such as drug delivery systems for cancer therapy, and scaffolds in wound healing and soft tissue engineering.Master Thesis Peptide Hydrogels Containing Cell Attachment Molecules(Izmir Institute of Technology, 2019) Uysal, Berk; Top, Ayben; Top, AybenIn this study, peptides with sequences and notations as KLELKLELKLEL (KLEL), KLDVKLDVKLDV (KLDV), KLDVKLDVKLKV (KLKV1), KLKVKLDVKLKV (KLKV2), KLKVKLKVKLKV (KLKV3) were synthesized using solid phase peptide synthesis (SPPS) method based on Fmoc chemistry. Reverse phase HPLC and MALDI-TOF mass spectroscopy characterization methods were used to assess the purity of the peptides. Three different synthesis procedures were tested, and it was found that employing DMF:DMSO at 1:1 ratio as a solvent increased purity of the resultant peptide. FTIR results indicated the presence of expected β-sheet secondary structure, as well as an interference band from TFA salts for all of the peptides. All the peptides formed hydrogels at pH 7.4 with 1 wt% concentration in deionized water (DIW). AFM results of these hydrogels indicated that KLKV1 and KLKV2 had fibrous morphology with a width of 5-20 nm and 7-18 nm respectively. KLDV and KLKV3 peptide hydrogels, on the other hand, exhibited globular structures, having sizes with 15-50 nm and 8-15 nm, respectively. Storage moduli (G’) of these hydrogels in DIW were obtained as ~860 ± 150 Pa, ~260 ± 60 Pa, ~210 ± 30 Pa and ~1850 ± 200 Pa for KLDV, KLKV1, KLKV2 and KLKV3 respectively. Of these peptides, only HCl salt of KLDV and KLKV1 peptides more readily formed hydrogels in PBS but at 1.5 wt% concentration. G’ values of these KLDV and KLKV1 hydrogels were determined as ~1810 ± 850 Pa and ~700 ± 230 Pa, respectively. Cell proliferation tests (CCK-8 assay) of KLDV and KLKV1 hydrogels were performed by using L929 mouse fibroblast cells. Empty wells (TCPS) were used as a control group. Cell proliferation was observed to be comparable for both select hydrogels and empty wells, suggesting possible applications of these hydrogels in tissue engineering.