Master Degree / Yüksek Lisans Tezleri
Permanent URI for this collectionhttps://hdl.handle.net/11147/3008
Browse
2 results
Search Results
Master Thesis Butyl Esters Production From Canola Oil Over Heterogeneous Base Catalysts(01. Izmir Institute of Technology, 2021) Akın, Oğuzhan; Şeker, Erol; Şeker, Erol; Şeker, Erol; 01. Izmir Institute of Technology; 03.02. Department of Chemical Engineering; 03. Faculty of EngineeringIn this study, transesterification reaction of canola oil with butanol over calcium oxide alumina catalyst was investigated with varying butanol:lipid molar ratios, catalyst amount and reaction time. Catalysts were prepared with the single step sol-gel method, and the activity of synthesized catalysts were investigated for two different forms of catalysts as powder and structured form. In the case of powdered catalysts, at butanol:lipid molar ratios of 9 and 24 with 6 wt% of lipids as catalyst amount, leaded 32% and 45% butyl esters yield in 1 hour. On the other hand, ~70% butyl esters yield has obtained at butanol:lipid molar ratios of 48 and 60 for the reaction time of 1 hour, while 89% yield had achieved when the reaction lasted for 4 hours at butanol:lipid molar ratio of 48. The necessity of mild basic strength and high butanol:lipid molar ratio was found to obtain high butyl esters yield. At high butanol lipid ratios of 48 and 60, it was observed that glycerolysis reaction occurs and promotes reverse transesterification reactions in first 30 minutes of the experiments. In the case of structured catalysts, lower butyl esters yields than powder catalysts were obtained, yet they eliminated the need for catalysts separation step in the experiments. Reusability tests showed that catalyst activity has decreased due to calcium ion leaching in the first hour of reaction and kept its activity constant for the rest of the reaction.Master Thesis Biofuels Production Using Canola Oil Over Heterogeneous Catalysts(Izmir Institute of Technology, 2017) Özdoğru, Bertan; Şeker, Erol; Şeker, Erol; 03.02. Department of Chemical Engineering; 03. Faculty of Engineering; 01. Izmir Institute of TechnologyThe goal of this study was to investigate the activity of Ni loaded on Al2O3-SiO2 supports prepared with different acids for the production of biofuel grade compounds while using canola oil as our feedstock. While keeping the reaction conditions constant, catalyst preparation parameters such as aluminum concentration, nickel concentration, calcination temperature, and acid types investigated with statistical methods by constructing Box Behnken design using three continuous parameters with two levels and one categorical parameter with three level. Responses considered in this study were aldehyde, ester, organic acid and other compound yields calculated from the GC-MS analysis. After ANOVA analysis, empirical models calculated from this analysis used to optimize the catalyst preparation parameters. Three catalysts, one for each acid type, selected to investigate the validity of our model. Analysis did on these catalysts have shown that both 0% Ni/25% Al2O3-75% SiO2 w/H2SO4 at 900oC and 20% Ni/75% Al2O3-25% SiO2 w/H3PO4 at 900oC catalysts gave good ester yields with good organic acid utilization. 20% Ni/75% Al2O3-25% SiO2 w/H3PO4 at 900oC catalyst was exceptional in ester selectivity aspect while 0% Ni/25% Al2O3-75% SiO2 w/H2SO4 at 900oC catalyst was in organic acid utilization aspect. Presence of aluminum phosphate crystal phase observed with XRD resulted in 20% Ni/75% Al2O3-25% SiO2 w/H3PO4 at 900oC catalyst having the highest selectivity towards ester production. Combination of weak and strong acid sites increased the organic acid selectivity while lowering the selectivity towards esters for 0% Ni/25% Al2O3-75% SiO2 w/H2SO4 at 900oC catalyst. From the low organic acid utilization observed with 10% Ni/25% Al2O3-75% SiO2 w/HNO3 at 500oC and, 10% Ni/50% Al2O3-50% SiO2 w/H2SO4 at 700oC catalysts which had high amounts of weak acid sites, it could be said that organic acids can only be reacted over strong acid sites.