  • Master Thesis
    Mechanistic Investigation of Carbon Dioxide Hydrogenation on Bimetallic Iron-Cobalt Surfaces by Density Functional Theory
    (2023) Kızılkaya, Ali Can; Kızılkaya, Ali Can; 03.02. Department of Chemical Engineering; 03. Faculty of Engineering; 01. Izmir Institute of Technology
    Küresel CO2 emisyonundaki artışa bağlı olarak iklim değişikliği, yalnızca CO2 üretiminin azaltılmasındaki önemi artırmakla kalmadı, aynı zamanda katalitik CO2 dönüşümü yoluyla kimyasalların ve yakıtların üretiminde kullanılmasının önemini de artırdı. Aktif ve seçici katalizörlerin rasyonel tasarımı, bu proseslerin endüstriyel uygulamalarına yönelik kritik öneme sahiptir. Bu tezde, C1 hidrokarbonların üretimi için CO2 hidrojenasyonunun mekanizmasını araştırmak ve FeCo bimetalik katalizörlerin (111) yüzeyindeki yapı-aktivite ilişkisinin atomik düzeyde anlaşılmasını sağlamak ve tasarıma rehberlik etmek için ilk prensiplere dayalı hesaplamalı bir çalışma yapıldı. Bu tezde, fcc-Co(111) ve Fe-katkılı Co(111) [FeCo(111)] yüzeyleri üzerinde CO2 hidrojenasyonunun C1 hidrokarbonlara verdiği temel reaksiyonların kinetiği, yoğunluk fonksiyonel teorisi (YFT) kullanılarak karşılaştırıldı. Araştırmamız Fe'nin Co(111) yüzeyine eklenmesi ile birlikte, CO2 aktivasyonunu desteklemesine rağmen genel reaksiyon hızını hafifçe azalttığını ortaya çıkardı. 1 ML Fe-katkılı Co(111) yüzeyinin daha düşük atomik H kapsamaları ve daha yüksek aktivasyon bariyerleri nedeniyle hidrojenasyon reaksiyonlarını engellemesi Fe'nin Lewis bazik karakterine atfedilmiştir. Fe'in katılması temel olarak kobalt yüzeylerinden oksijenin ayrılmasını engellemektedir. Bu nedenle, Fe katkısının, CO2 hidrojenasyonu sırasında bimetalik FeCo katalizörleri üzerinde oksidik fazların oluşumunu teşvik etmesi beklenmektedir.
  • Master Thesis
    Selective Hydrogenation of Citral Over Mesoporous Ru/Tio2 Catalysts
    (Izmir Institute of Technology, 2013) Hassan, Hassanain Abbas; Yılmaz, Selahattin; Yılmaz, Selahattin; 03.02. Department of Chemical Engineering; 03. Faculty of Engineering; 01. Izmir Institute of Technology
    The liquid phase citral hydrogenation was investigated over Ru/SiO2, Ru/TiO2 and Ru/TiO2/SiO2 catalysts. TiO2/SiO2 supports were prepared by sol-gel deposition, impregnation and absorption methods. The effect of the supports and catalyst reduction temperature, 300 ï‚°C (LTR) and 450 ï‚°C (HTR) on citral conversion and selectivity to unsaturated alcohols were examined. A well-defined crystalline anatase phase was only observed on the support prepared by absorption method, TiO2/SiO2-ABS. A high dispersion and interaction of Ru were observed over TiO2 for Ru/TiO2. Ru/TiO2/SiO2-ABS also displayed similar properties but to a lower extent. Ru/TiO2/SiO2-ABS catalyst showed the highest citral conversion (57.7 %) at LTR among the different Ru/TiO2/SiO2 catalysts. Its selectivity to UA was also high (70.2 %). This was attributed to a better metal support interaction and dispersion obtained by this method. However, a selectivity of 62.6 % was obtained over Ru/TiO2. Activity of the catalysts was mostly observed to decrease as reduction temperature increased from 300 ï‚°C to 450 ï‚°C. Citral conversion decreased from 57.7 % to 42.3 % over Ru/TiO2/SiO2-ABS. However, selectivities to unsaturated alcohol (nerol and geraniol) over Ru/TiO2 and Ru/TiO2/SiO2 catalysts were increased at HTR, reaching about 80 %. This was suggested to be due to more interaction of TiO2 with the Ru (strong metal support interaction). There was no significant change in the selectivity to UA obtained at HTR for Ru/SiO2. This was related to the inert nature of SiO2.