Master Degree / Yüksek Lisans Tezleri
Permanent URI for this collectionhttps://hdl.handle.net/11147/3008
Browse
3 results
Search Results
Master Thesis Sb2se3 Absorber Layered Solar Cell Fabrication and Characterization(01. Izmir Institute of Technology, 2021) Kurtuldu, Seher Hazal; Aygün, Gülnur; Tarhan, Enver; Tarhan, Enver; Aygün Özyüzer, Gülnur; Tarhan, Enver; 01. Izmir Institute of Technology; 04.05. Department of Pyhsics; 04. Faculty of ScienceThin-film antimony selenide (Sb2Se3) solar cells have gained attention as a high-potential photovoltaic technology around the world. Outstanding features like a high absorption coefficient, a suitable direct bandgap, and good hole mobility make Sb2Se3 a promising absorber material for solar cell applications. It has demonstrated a very rapid growth reaching 9.2% power conversion efficiency (PCE) in only 7 years after intensive studies. In the present thesis, first of all Sb2Se3 thin films were deposited on soda lime glasses (SLGs) and investigated using energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), scanning electron microscopy (SEM), spectrophotometry and Raman spectroscopy. Structural and optical studies were carried out depending on the thickness, used argon (Ar) gas flow rate and post-annealing temperature of the Sb2Se3 films in order to optimize the absorber layer to be used in solar cell. This study revealed that key parameters such as band gap energy and crystal structure of the Sb2Se3 thin films affected by the thickness, Ar gas flow rate during deposition and post-annealing temperature. In addition, oxide phase formation was also found to be related to these growth parameters. Finally, SLG/ITO/Zn(O,S)/Sb2Se3/Ag for superstrate configuration and both SLG/Mo/Sb2Se3/CdS/ITO and SLG/Mo/Sb2Se3/CdS/ZnS/ITO devices fabricated for substrate configuration solar cells. Since Zn(O,S)/Sb2Se3 heterojunction has not been studied before in the literature, this study will be the first. At the end of the electrical analysis, the best conversion efficiency of 3.9% was achieved by the solar cell with the substrate configuration.Master Thesis Anti-Reflective and Optical Transparent Coatings for Thin Film Solar Cells and Glasses(Izmir Institute of Technology, 2020) Özyüzer, Lütfi; Özyüzer, Lütfi; Özyüzer, Lütfi; 04.05. Department of Pyhsics; 04. Faculty of Science; 01. Izmir Institute of TechnologyAntireflective coatings in some implementation necessary for the decreasing surface reflection, but in some applications also for increasing transmittance. Incident radiation on the surface of the optical material is divided into transmitted, reflected, scattered, and absorbed proportions, and the proportion of current energy that deployed among them is defined by RI (refraction indices). Solar panels made from crystalline or polycrystalline silicon, but another type of solar panel is a thin-film solar panel. Thin-film technology has several advantages, such as low material consumption, which leads to cost savings to production, the ability to absorb diffused solar radiation, a relatively high efficiency (up to 20%), long service life (efficiency decreases by 10-15% of the initial efficiency). For all types of photovoltaic devices, energy loss is an important issue. Single-layer and two-layer antireflection coatings with a low refractive index, coated and uncoated (SiO2) thin-film with the sol-gel method were prepared and compared in terms of performance and continuity. The photocatalytic performance of (SiO2) thin films in 1, 2, 3, 4, 5 and 24 hours was defined with methylene blue dye solution (20 mL) under UV source and was illuminated by it. The I-V characteristics curve of solar cells for small and large area was learned and increasing efficiency was observed. Adhesion tests in this study was applied by tape tests on substrates of glass. As a result, the field tests of small and large area glasses coated solar panels were realized, the low reflectance and high efficiency were obtained.Master Thesis Efficiency Studies of Cu2znsns2 Thin Film Solar Cell(Izmir Institute of Technology, 2018) Meriç, Ece; Aral, Gürcan; Özyüzer, Lütfi; Özyüzer, Lütfi; Aral, Gürcan; 04.05. Department of Pyhsics; 04. Faculty of Science; 01. Izmir Institute of TechnologyCu2ZnSnS4 (CZTS) is a promising candidate as an absorber layer for thin film solar cells due to not only its low cost but also nontoxic properties contrary to alternative materials such as CdTe and Cu(In,Ge)Se2 (CIGS). Recently, CZTS and similar chalcogenides have attracted remarkable attention because of their suitable properties. In my thesis; I studied the efficiency of Cu2ZnSnS4 thin film solar cells for various stoichiometric cases. Besides, the effect of back contact, buffer layer thickness and sulfurization time were investigated. CZTS thin films were fabricated by DC magnetron sputtering method on Molybdenum (Mo) coated Soda Lime Glass (SLG) and Ti foil substrates. Cu, Sn, Zn, Cu layers were, respectively, deposited on the substrates, and then sulfurization process was followed as the second step in the growth process to obtain a desirable CZTS formation. The as grown CZTS structure was investigated using Raman and X-Ray Diffraction (XRD) spectroscopies. Scanning electron microscopy (SEM) was used to investigate the surface morphology of the films. Energy dispersive spectroscopy (EDS) was used to define the chemical structure of the surface of the films. Next, a CdS buffer layer was deposited on CZTS absorber layer using CBD method at 85oC for varying times (60, 75 and 90 min). Then, ZnO and Al doped ZnO (AZO) layers were deposited on CdS. J-V curves were obtained for SLG/Mo/CZTS/CdS/ZnO/AZO solar cell structure. The photovoltaic characteristic of solar cells was studied and their dependence on CdS deposition time were found. Among all the device we produced, the highest efficiency was obtained for the device with the lowest CdS deposition time. In addition; effect of sulfurization time on the solar cell conversion efficiency was studied.