Master Degree / Yüksek Lisans Tezleri
Permanent URI for this collectionhttps://hdl.handle.net/11147/3008
Browse
2 results
Search Results
Master Thesis 1-Octanol Dehydration on Al2o3-Sio2 Catalyst(01. Izmir Institute of Technology, 2021) Şeker, Erol; Uçar, Beyza; Şeker, Erol; 03.02. Department of Chemical Engineering; 01. Izmir Institute of Technology; 03. Faculty of EngineeringBu çalışmada, heterojen asit katalizörün 1-oktanol dehidrasyonunda, ürün dağılımına etkisi araştırılmıştır. Kullanılan katalizörler sol-jel yöntemiyle sentezlenmiştir. Sentezlenen katı asit katalizörler ağırlıkça farklı oranlarda (25%-75%, 50%-50% ve 75%-25%) Al2O3-SiO2 katalizörleriydi. Ayrıca, sentezlenen Al2O3-SiO2 katalizörlerin kalsinasyon sıcaklıkları 500 ̊C, 700 ̊C ve 900 ̊C idi. Bu çalışmanın amacı, Al2O3-SiO2 katalizörlerin asidik-bazik özelliklerini ve birincil alkol dehidrasyonu üzerindeki etkisini anlamaktır. Kullanılan bütün katalizörler için dehidrasyon reaksiyonu 150 ̊C ve reaksiyon süresi 4 saat olarak devam etti. Ürünler ve var olan miktarı GC-MS analizi ile belirlenmiştir. Buna ek olarak, katalizörlerin asidik ve bazik özellikleri NH3-TPD ve CO2-TPD analizleri ile açıklanmıştır. Ayrıca katalizörlerin kristalografisi, XRD sonuçlarına göre belirtilmiştir. Bu çalışma, katalizörlerin bileşiminin ve uygulanan kalsinasyon sıcaklıklarının, reaksiyon yollarını etkileyen asidik-bazik kuvvetleri üzerinde etkili olduğunu ortaya koymuştur. Bunun sonucunda ürün dağılımı ve genel dönüşüm değerlendirilmiştir. Ana ürünler oksalik asit 2-etilheksil tetradesil ester, oktil eter, esterler (Formik asit, oktil ester, Asetik asit, oktil ester ve Heptanoik asit, oktil ester) ve oktanal idi. Ürün dağılımının esas olarak Al2O3-SiO2 katalizörlerinin asidik ve bazik güclerine bağlı olduğu gösterildi.Master Thesis Biofuels Production Using Canola Oil Over Heterogeneous Catalysts(Izmir Institute of Technology, 2017) Özdoğru, Bertan; Şeker, Erol; Şeker, Erol; 03.02. Department of Chemical Engineering; 03. Faculty of Engineering; 01. Izmir Institute of TechnologyThe goal of this study was to investigate the activity of Ni loaded on Al2O3-SiO2 supports prepared with different acids for the production of biofuel grade compounds while using canola oil as our feedstock. While keeping the reaction conditions constant, catalyst preparation parameters such as aluminum concentration, nickel concentration, calcination temperature, and acid types investigated with statistical methods by constructing Box Behnken design using three continuous parameters with two levels and one categorical parameter with three level. Responses considered in this study were aldehyde, ester, organic acid and other compound yields calculated from the GC-MS analysis. After ANOVA analysis, empirical models calculated from this analysis used to optimize the catalyst preparation parameters. Three catalysts, one for each acid type, selected to investigate the validity of our model. Analysis did on these catalysts have shown that both 0% Ni/25% Al2O3-75% SiO2 w/H2SO4 at 900oC and 20% Ni/75% Al2O3-25% SiO2 w/H3PO4 at 900oC catalysts gave good ester yields with good organic acid utilization. 20% Ni/75% Al2O3-25% SiO2 w/H3PO4 at 900oC catalyst was exceptional in ester selectivity aspect while 0% Ni/25% Al2O3-75% SiO2 w/H2SO4 at 900oC catalyst was in organic acid utilization aspect. Presence of aluminum phosphate crystal phase observed with XRD resulted in 20% Ni/75% Al2O3-25% SiO2 w/H3PO4 at 900oC catalyst having the highest selectivity towards ester production. Combination of weak and strong acid sites increased the organic acid selectivity while lowering the selectivity towards esters for 0% Ni/25% Al2O3-75% SiO2 w/H2SO4 at 900oC catalyst. From the low organic acid utilization observed with 10% Ni/25% Al2O3-75% SiO2 w/HNO3 at 500oC and, 10% Ni/50% Al2O3-50% SiO2 w/H2SO4 at 700oC catalysts which had high amounts of weak acid sites, it could be said that organic acids can only be reacted over strong acid sites.