  • Article
    Citation - WoS: 11
    Citation - Scopus: 13
    Effect of Cnt Incorporation on Pan/Ppy Nanofibers Synthesized by Electrospinning Method
    (TÜBİTAK, 2020) İnce Yardımcı, Atike; Selamet, Yusuf; Tanoğlu, Metin; Tanoğlu, Metin; Yılmaz, Selahattin; Yılmaz, Selahattin; Selamet, Yusuf; 03.02. Department of Chemical Engineering; 03.10. Department of Mechanical Engineering; 04.05. Department of Pyhsics; 03. Faculty of Engineering; 04. Faculty of Science; 01. Izmir Institute of Technology
    In this study, carbon nanotubes (CNTs) added polyacrylonitrile/polypyrrole (PAN/PPy) electrospun nanofibers were produced. Average diameters of the nanofibers were measured as 268 and 153 nm for 10 and 25 wt% of PPy contents, respectively. A relatively higher strain to failure values (23.3%) were observed for the low PPy content. When as-grown CNTs (1 and 4 wt%) were added into the PAN/PPy blends, disordered nanofibers were observed to form within the microstructure. To improve the interfacial properties of CNTs/PAN/PPy composites, CNTs were functionalized with H2SO4/HNO3/HCl solution. The functionalized CNTs were well dispersed within the nanofibers and aligned along the direction of nanofibers. Therefore, beads formation on nanofibers decreased. The impedance of the nanofibers was found to decrease with the PPy content and CNT addition. These nanofibers had a great potential to be used as an electrochemical actuator or a tissue engineering scaffold.
  • Article
    Citation - WoS: 74
    Humidity Sensing Properties of Zno-Based Fibers by Electrospinning
    (Elsevier Ltd., 2011) Horzum Polat, Nesrin; Taşçıoğlu, Didem; Okur, Salih; Demir, Mustafa Muammer; Demir, Mustafa Muammer; 04.05. Department of Pyhsics; 03.09. Department of Materials Science and Engineering; 03. Faculty of Engineering; 04. Faculty of Science; 01. Izmir Institute of Technology
    Zinc oxide (ZnO) based fibers with a diameter of 80-100 nm were prepared by electrospinning. Polyvinyl alcohol (PVA) and zinc acetate dihydrate were dissolved in water and the polymer/salt solution was electrospun at 2.5 kV cm-1. The resulting electrospun fibers were subjected to calcination at 500 °C for 2 h to obtain ZnO-based fibers. Humidity sensing properties of the fiber mats were investigated by quartz crystal microbalance (QCM) method and electrical measurements. The adsorption kinetics under constant relative humidity (RH) between 10% and 90% were explained using Langmuir adsorption model. Results of the measurements showed that ZnO-based fibers were found to be promising candidate for humidity sensing applications at room temperature.