  • Article
    Citation - WoS: 8
    Citation - Scopus: 8
    Comparing Compression Deformation and Rate Sensitivity of Additively Manufactured and Extruded-Annealed 316l Alloys
    (Springer, 2021) Enser, Samed; Yavaş, Hakan; Arslan Hamat, Burcu; Aydın, Hüseyin; Kafadar, Gülten; Tanrıkulu, A. Alptuğ; Zeytin Kazdal, Havva; Öztürk, Fahrettin; Güden, Mustafa
    The deformation behavior of a selective-laser-melt-processed 316-L alloy (SLM-316L) under compression was determined together with a commercial annealed-extruded 316L alloy bar (C-316L) for comparison. Strain rate jump tests and hardness tests on the untested and compression tested samples were also performed. Extensive microscopic observations on the deformed and undeformed samples showed a twinning-dominated deformation in SLM-316L, similar to twinning-induced-plasticity steels, while a martensitic transformation-dominated deformation in C-316L alloy, similar to transformation-induced-plasticity steels. Within the studied quasi-static strain rate regime, the measured higher strain rate sensitivity of SLM-316L was ascribed to the lower distances between the nano-twins, in the level of 100 nm, than the distances between martensite plates, in the level of 1000 nm. A higher hardness increase in the martensite transformation region as compared with the twinned region proved the higher work hardening of C-316L. The hardness tests in the micron and sub-micron levels further confirmed the previously determined relatively low resistances of the dislocation cell walls (sub-grain) to the dislocation motion in SLM-316L alloy.
  • Article
    Citation - WoS: 8
    Citation - Scopus: 9
    The Increased Compression Strength of an Epoxy Resin With the Addition of Heat-Treated Natural Nano-Structured Diatom Frustules
    (SAGE Publications Inc., 2017) Zeren, Doğuş; Güden, Mustafa
    Natural diatom frustules composing nanometer size silica particles were heat-treated at temperatures between 600 and 1200℃ for 2 h and used as filler/reinforcing agent (15 wt%) in an epoxy resin. The opal structure of as-received natural diatom frustules was transformed into cristobalite after the heat-treatment above 900℃. The epoxy resin test samples reinforced with heat-treated and as-received frustules and neat epoxy test samples were compression tested at the quasi-static strain rate of 7 × 10−3 s−1. The results showed that the inclusion of the frustules heat-treated at 1000℃ increased the compressive yield strength of the resin by 50%, while the addition of the diatom frustules heat-treated above and below 1000℃ and the as-received frustules increased the strength by ∼25% and 16%, respectively. The heat treatment above 1000℃ decreased the surface area of the frustules from 8.23 m2 g−1 to 3.46 m2 g−1. The cristobalite grains of the frustules heat-treated at 1000℃ was smaller than 100 nm, while the grain size increased to ∼500 nm at 1200℃. The increased compressive stresses of the resin at the specific heat treatment temperature (1000℃) were ascribed to nano size crystalline cristobalite grains. The relatively lower compressive stresses of the epoxy resin filled with frustules heat-treated above 1000℃ were attributed to the micro-cracking of the frustules that might be resulted from higher density of the cristobalite than that of the opal and accompanying reduction of the surface area and the surface pore sizes that might impair the resin-frustule interlocking and intrusion.