WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7150
Browse
4 results
Search Results
Now showing 1 - 4 of 4
Article Citation - WoS: 36Citation - Scopus: 36Surfactant-Assisted Formation of Organophilic Ceo2 Nanoparticles(Elsevier Ltd., 2012) Tunusoğlu, Özge; Muñoz-Espí, Rafael; Akbey, Ümit; Demir, Mustafa MuammerWe report a simple one-pot method to prepare organically functionalized CeO 2 nanoparticles by controlled chemical precipitation. The particles were nucleated by mixing aqueous solutions of Ce(NO 3) 3·6H 2O and ammonia at room temperature. Different small organic molecules were chosen as capping agents and injected into the reaction medium at the beginning of the synthesis: 3-(mercaptopropyl) trimethoxy silane (MPS), hexadecyltrimethyl ammonium bromide (CTAB), 3-mercapto propionic acid (3-MPA), and thioglycolic acid (TGA). The resulting nanocrystals were quasi-spherical and had a narrow mean size distribution with an average size smaller than 10nm. Dynamic nuclear polarization enhanced NMR (DNP-NMR) and FTIR measurements suggested a chemical grafting of the surfactant and a homogeneous surface modification. The colloidal stabilities were characterized by dynamic light scattering and zeta potential measurements. The stabilization by aliphatic groups was tested with a frequently used hydrophobic monomer, methyl methacrylate. According to the results, CTAB is the most effective of the used stabilizing surfactant. The mechanism of formation of the organophilic CeO 2 nanoparticles is discussed.Article Citation - WoS: 64Citation - Scopus: 67Hierarchically Structured Metal Oxide/Silica Nanofibers by Colloid Electrospinning(American Chemical Society, 2012) Horzum Polat, Nesrin; Mun˜oz-Espí, Rafael; Glasser, Gunnar; Demir, Mustafa Muammer; Landfester, Katharina; Crespy, DanielWe present herein a new concept for the preparation of nanofibrous metal oxides based on the simultaneous electrospinning of metal oxide precursors and silica nanoparticles. Precursor fibers are prepared by electrospinning silica nanoparticles (20 nm in diameter) dispersed in an aqueous solution of poly(acrylic acid) and metal salts. Upon calcination in air, the poly(acrylic acid) matrix is removed, the silica nanoparticles are cemented, and nanocrystalline metal oxide particles of 4-14 nm are nucleated at the surface of the silica nanoparticles. The obtained continuous silica fibers act as a structural framework for metal oxide nanoparticles and show improved mechanical integrity compared to the neat metal oxide fibers. The hierarchically nanostructured materials are promising for catalysis applications, as demonstrated by the successful degradation of a model dye in the presence of the fibers.Article Citation - WoS: 73Citation - Scopus: 73Toward Transparent Nanocomposites Based on Polystyrene Matrix and Pmma-Grafted Ceo 2 Nanoparticles(American Chemical Society, 2011) Parlak, Onur; Demir, Mustafa MuammerThe association of transparent polymer and nanosized pigment particles offers attractive optical materials for various potential and existing applications. However, the particles embedded into polymers scatter light due to refractive index (RI) mismatch and reduce transparency of the resulting composite material. In this study, optical composites based on polystyrene (PS) matrix and poly(methyl methacrylate) (PMMA)-grafted CeO 2 hybrid particles were prepared. CeO 2 nanoparticles with an average diameter of 18 ± 8 nm were precipitated by treating Ce(NO 3) ·6H 2O with urea in the presence of a polymerizable surfactant, 3-methacyloxypropyltrimethoxy silane. PMMA chains were grafted on the surface of the nanoparticles upon free radical in situ solution polymerization. While blending of unmodified CeO 2 particles with PS resulted in opaque films, the transparency of the composite films was remarkably enhanced when prepared by PMMA-grafted CeO 2 hybrid particles, particularly those having a PMMA thickness of 9 nm. The improvement in transparency is presumably due to the reduction in RI mismatch between CeO 2 particles and the PS matrix when using PMMA chains at the interface.Article Citation - WoS: 11Citation - Scopus: 11Effect of Alkali Metal Hydroxides on the Morphological Development and Optical Properties of Ceria Nanocubes Under Hydrothermal Conditions(American Scientific Publishers, 2011) Kepenekçi, Özlem; Eanes, Mehtap; Demir, Mustafa MustafaNanocrystalline cerium(IV) oxide (CeO2, ceriaceria) particles were produced via the hydrothermal treatment of cerium nitrate hexahydrate with various alkali metal hydroxides (MOH: M = Li, Na, K). Experimental conditions such as [MOH], reaction temperature, and reaction time were studied. Particle morphology as well as size of crystallites was precisely controlled by choice of experimental conditions. While rod-shaped particles were obtained at 120 C, well-defined nanocubes were formed at higher temperatures regardless of the choice of MOH. Examination of particle growth kinetics, in the final stages of crystallization, showed that particle growth rate is controlled by two different mechanisms. Grain boundary diffusion controls the particle growth in the presence of NaOH with an activation energy of 113.8 kj/mol and surface diffusion for LiOH ad KOH with the activation energy of 43.0–150.9 kj/mol, respectively. In addition, the particles exhibit strong violet and blue emissions at 400 nm and 370 nm. The former emission originates from excitation of a wide band gap of CeO2. The latter one is attributed to the trivalency of the cerium ion and appears to be sensitive to all the experimental conditions studied. Both extending reaction time and increasing temperature reduce the intensity of the 370 nm emission and increase the intensity of the 400 nm emission.