WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7150
Browse
5 results
Search Results
Now showing 1 - 5 of 5
Article Impact of Titania Phase Structure and Surface Reactivity on the Photocatalytic Degradation of Various Dyes and Textile Wastewater(National Institute of Science Communication and Policy Research, 2023) Yurtsever, Hüsnü Arda; İloğlu, Onur; Çiftçioğlu, MuhsinTitania (TiO2) powders have been prepared by precipitation method in different precipitation media which contain sulfate, nitrate or organic species. Photocatalytic degradation of different dyes and a real textile wastewater have been conducted with these powders along with commercial powder Degussa P25 for comparison. Ethyl alcohol (organic medium), sulfuric acid (sulfate medium) and nitric acid (nitrate medium) have been used to dissolve titanium precursor for the precipitation of TiO2 in ammonia solution. UV-Vis DRS and XPS results indicate that S doping in sulfate medium precipitated powder and N doping in nitrate medium precipitated powder has been occurred and the presence of S or N containing impurities on the grain boundaries have been improved light absorption of TiO2 significantly. However, these powders have exhibited low surface reactivities. The highest surface reactivity has been obtained with the powder precipitated in organic medium which also has the highest crystallite sizes (76 nm rutile and 34 nm anatase crystallites) with relatively low rutile weight percentage (10.0%). The surface-normalized rate constants of this powder are 0.02038 min-1.m-2 in real textile wastewater degradation and 0.0161 min-1.m-2 in methyl orange degradation, which are 0.01563 and 0.0091 min-1.m-2, respectively, for Degussa P25. Results have shown that this powder show 30-70% higher surface reactivities compared to Degussa P25. The main structural difference of organic medium precipitated powder and Degussa P25 has been found to be the anatase-rutile weight ratio and crystallite size of rutile phase whereas band gap energy of Degussa P25 is lower and other properties are not significantly different.Article Citation - WoS: 19Citation - Scopus: 22Optimization of the Associative Growth of Novel Yoghurt Cultures in the Production of Biomass, Ss-Galactosidase and Lactic Acid Using Response Surface Methodology(Elsevier Ltd., 2009) Tarı, Canan; Üstok, Fatma Işık; Harsa, Hayriye ŞebnemThe associative growth of Streptococcus thermophilus 95/2 (St 95/2) and Lactobacillus delbrueckii ssp. bulgaricus 77 (Lb 77) isolated from the Toros mountain region of Turkey was investigated with respect to lactic acid, biomass and β-galactosidase enzyme production using response surface methodology (RSM). The ratio (St 95/2:Lb 77) of the strains and media formulation had significant effect on all responses (p < 0.001). The predicted enzyme activity (2.14 U mL-1), lactic acid (22.50 g L-1) and biomass (7.11 g L-1) production at optimum conditions were very close to the actual experimental values (2.14 U mL-1, 22.94 g L-1 and 7.86 g L-1, respectively). The optimum conditions were to use these cultures in a ratio of 1.66:1.62 (St 95/2:Lb 77) in a medium containing whey (5%), corn steep liquor (4%), potassium phosphate (2%) and peptone (2%) at 43 °C for 8 h. The associative growth provided 6.4% and 39% more β-galactosidase activity and 8.73% and 44% more lactic acid compared with the results obtained using pure St 95/2 and Lb 77 strains, respectively.Article Citation - WoS: 10Citation - Scopus: 10Determination of the Particle Interactions, Rheology and the Surface Roughness Relationship for Dental Restorative Ceramics(Elsevier Ltd., 2009) Kes, Mürşide; Polat, Hürriyet; Keleşoğlu, Serkan; Polat, Mehmet; Aksoy, GökhanThe effect of inter-particle interactions on the slurry properties and the final surface roughness of the dental ceramic restoratives was investigated. A commercial dental ceramic powder, IPS Empress 2 veneer, was used as the raw material. The magnitudes of the particle-particle interactions were computed by the DLVO theory for the ceramic slurries of different electrolyte solutions (0.1 M, 0.25 M, 0.5 M, 0.75 M, 1 M NaCl and CaCl2). As expected, the energies of particle-particle interactions were influenced significantly by the presence of electrolytes. These computations demonstrated that addition of electrolytes leads to a progressive depression of the repulsive double layer forces. The absence of these forces should inevitably lead to agglomeration caused by the ever-present van der Waals forces. The rheological measurements carried out using the slurries with same solution properties supported the findings of the DLVO computations. It was found that dental ceramic slurries showed a Newtonian behavior in the absence of electrolytes, which is indicative of little or no agglomeration in the slurry. On the other hand, the same slurries displayed a non-Newtonian, shear thinning behavior in the presence of electrolytes which can be attributed to agglomeration or gelation. Roughness of the ceramic surfaces produced from these slurries was studied by SEM analysis and profilometer measurements. Contact angle studies were also carried out on the same surfaces. It was observed that the surface became rougher initially with electrolyte addition to a maximum, most probably due to formation of isolated agglomerates due to a reduction of the repulsive double layer forces. After reaching a maximum, surface roughness decreased to a much lower value with further increase in electrolyte concentration. This was most probably caused by the formation of a relatively homogeneous, gel-like structure within the extensively agglomerated slurry due to a complete collapse of the double layer.Conference Object Citation - WoS: 1Citation - Scopus: 1Modification of Surface Morphology of Uhmwpe for Biomedical Implants(Materials Research Society, 2007) Öztarhan, Ahmet; Sokullu Urkaç, Emel; Kaya, Nusret; Yenigül, Mesut; Tıhmınlıoğlu, Funda; Ezdeşir, Ayhan; Zimmerman, Robert; Budak, Satılmış; Muntele, C.; Chhay, Bopha; Ila, Daryush; Oks, Efim; Nikolaev, Alexey; Tek, Zekai; Eltem, RenginUltra High Molecular Weight Polyethylene (UHMWPE) samples were implanted with metal and metal-gas hybrid ions (Ag, Ag+N, C+H, C+H+Ar, Ti+O) by using improved MEVVA Ion implantation technique [1,2]. An extraction voltage of 30 kV and influence of 1017 ions/cm2 were attempted in this experiment, to change their surface morphologies in order to understand the effect of ion implantation on the surface properties of UHMWPEs. Characterizations of the implanted samples with RBS , ATR - FTIR, spectra were compared with the un-implanted ones . Implanted and unimplanted samples were also thermally characterized by TGA and DSC. It was generally observed that C-H bond concentration seemed to be decreasing with ion implantation and the results indicated that the chain structure of UHMWPE were changed and crosslink density and polymer crystallinity were increased compared to unimplanted ones resulting in increased hardness. It was also observed that nano size cracks (approx.10nm) were significantly disappeared after Ag implantation, which also has an improved antibacterial effect. Contact angle measurements showed that wettability of samples increased with ion implantation. Results showed that metal and metal+gas hybrid ion implantation could be an effective way to improve the surface properties of UHMWPE to be used in hip and knee prosthesis.Article Citation - WoS: 12Citation - Scopus: 12Dispersion of Organophilic Ag Nanoparticles in Ps-Pmma Blends(Elsevier Ltd., 2015) Tüzüner, Şeyda; Demir, Mustafa Muammer.Abstract The preparation of stable composites with well-controlled particle location is one of the challenges in formulating new polymer/nanoparticle mixtures. In this study, cetyltriammonium bromide (CTAB)-capped monodisperse Ag nanoparticles were prepared and mixed with an equimass blend of polystyrene (PS) and poly(methyl methacrylate) (PMMA) in solution. The surface of the blend film without nanoparticles showed spherical pits with a size of 4.5 μm in diameter. The integration of CTAB-capped nanoparticles into the blend film developed surface bumps with a size of 0.4 μm in diameter. The organophilic Ag nanoparticles were distributed heterogeneously in the immiscible PS-PMMA blend. When the diameter of particle domains reached approximately 20 nm, particles were preferentially located at the interface of the PS and PMMA domains. Larger particle domains with a diameter of 90 nm were found to be in the PMMA-rich phase. Isothermal post-treatment of the PS-PMMA/Ag composite films directs the particle domains into PS domains. Thermodynamic factors that contribute to the observed morphologies are discussed.