Chemical Engineering / Kimya Mühendisliği
Permanent URI for this collectionhttps://hdl.handle.net/11147/14
Browse
3 results
Search Results
Article Citation - WoS: 4Citation - Scopus: 5Dynamic Heat of Adsorption of Water Vapour on Zeolitic Tuff and Zeolite 4a by Flow Microcalorimetry(Scibulcom Ltd., 2006) Ülkü, Semra; Balköse, Devrim; Ülkü, Semra; Alp, Burcu; Balköse, Devrim; 03.02. Department of Chemical Engineering; 03. Faculty of Engineering; 01. Izmir Institute of TechnologyIn this study a practical method for measurement of heat of adsorption of water vapour on adsorbents was developed to evaluate the feasibility of substitution of a zeolitic tuff with zeolite 4A in air drying and heat pumps. The change of heat of adsorption with inlet humidity of the air passing through the calorimeter was investigated. Samples were characterised by X-ray diffraction and thermal gravimetric analysis techniques. Specific heats of the zeolitic tuff and zeolite 4A were measured as 1.01 and 1.42 J/g K, respectively. Adsorption isotherms fitted to the Langmuir model with regression coefficient 0.93 and 0.94 with monolayer capacities, Xm 9.68% and 26.35% H 2O for the zeolitic tuff and zeolite 4A, respectively. The energy storage intensity was measured in the range 48-97 J/g and 464-201 J/g for the tuff and zeolite 4A, respectively. Heat of adsorption of zeolite decreased with surface coverage and it was in the range 1750-2835 and 1104-2640 J/g H 2O for the zeolitic tuff and zeolite 4A, respectively.Article Citation - WoS: 8Citation - Scopus: 8Water Vapour Adsorption on Organic and Inorganic Polymers(Springer Verlag, 2003) Balköse, Devrim; Özkan, Fehime; Balköse, Devrim; Ülkü, Semra; Ülkü, Semra; Özkan, Seher Fehime; 03.02. Department of Chemical Engineering; 03. Faculty of Engineering; 01. Izmir Institute of TechnologyWater vapour adsorption on polymers affects their processing behaviour and useful properties. Water vapour adsorption on organic polymers, silk, Nylon 6 fibres in undrawn and permanent set forms, polyester micro fibres, plasticised PVC films with 60 phr dioctylphthalate (OOP) and inorganic polymer sepiolite particles were investigated in this study. The materials were examined using the BET equation. The surface areas of silk, cast Nylon 6 and muss Nylon 6 were determined as 108, 46 and 23 m2 g-1, respectively. Sepiolite did not fit BET equation. Polyester and PVC adsorbed very small amounts of moisture.Article Citation - WoS: 47Citation - Scopus: 49Characterization of Hollow Chemical Garden Fibers From Metal Salts and Water Glass(Springer Verlag, 2002) Balköse, Devrim; Özkan, Fehime; Özkan, Seher Fehime; Ulutan, Sevgi; Balköse, Devrim; Ülkü, Semra; 03.02. Department of Chemical Engineering; 03. Faculty of Engineering; 01. Izmir Institute of TechnologyHollow fibers formed from water glass and metal salts of IIA(Ca), VIIB(Fe, Co, Ni) and IB(Cu) groups were characterised in this study. Fragile fibres obtained herein broke down into small pieces during isolation and drying. Quantitative information about morphology, chemical composition and surface structure of the fibres were obtained. The diameter and wall thickness of the fibers were around 50 μ and 3 μ. respectively. They had particulate inner and smooth outer surfaces. Fibers had variable composition with metal (II) oxide/SiO2 ratio in the range 0.31 to 1.02. While group VIIB metal (II) fibres were amorphous, group IIA and IB metal (II) fibers were partially crystalline All the fibres had pores both in micro pore and meso pore region. The B.E.T. surface area fron N2 adsorption data was in the range of 10-249 m3 g-1 and 8-176 m2 g-1 from Langmuir an B.E.T. models respectively.