Chemical Engineering / Kimya Mühendisliği
Permanent URI for this collectionhttps://hdl.handle.net/11147/14
Browse
2 results
Search Results
Article Citation - WoS: 17Citation - Scopus: 19Effect of Compaction Pressure on Structural and Superconducting Properties of Bi-2223 Superconductors(Springer Verlag, 2010) Kocabaş, Kemal; Gökçe, Melis; Çiftçioğlu, Muhsin; Bilgili, ÖzlemIn this work, effects of compaction pressure on the structural and superconducting properties of BSCCO ceramic superconductors were investigated. The study was carried out on two systems which were, System I: Bi 1.7Pb 0.3Sr 2Ca 2Cu 3O y and System II: Bi 1.6Pb 0.3Ag 0.1Sr 2Ca 2Cu 3O y, respectively. Ceramic powders were prepared by conventional solid-state reaction method and sintered at 850°C after compaction at five different pressures in the 150-750 MPa range. Critical temperatures of samples were determined by resistivity-temperature determinations made by four-point probe method in liquid nitrogen conditions. XRD analysis was conducted by powder X-ray diffraction method. Morphology of the grains present in the samples were determined by using scanning electron microscope (SEM) photographs at 2 K× and 2.5 K× magnifications for System I and System II, respectively. Sintered densities of the superconducting ceramics were measured by Archimedes water displacement method and unit cell parameters were additionally obtained from XRD data. T c values for System I was determined to be in the 109-115 K with sample D having the highest T c of 115 K while T c varied in the 104-109 K range and sample B had the highest T c value of 109 K for System II. The transition width, which is a sign of the purity of the samples, was determined to be narrow for both systems. The data obtained from X-ray diffraction measurements have shown that 2223 high-T c phase was dominant in both systems. The determination of the optimum pellet compaction pressure for BSCCO ceramic superconductors was the main purpose of this work. The results of this work indicated that compaction at around 450 MPa improves the superconducting and structural properties of the BSCCO ceramic superconductors. © 2009 Springer Science+Business Media, LLC.Article Citation - WoS: 12Citation - Scopus: 12The Effect of Zn Substitution of Ca in Bipbsrcacuo Superconductors Sintered at 830°c(Springer Verlag, 2009) Kocabaş, Kemal; Şakiroğlu, Serpil; Çiftçioğlu, Muhsin; Ercan, İsmail; Epik, Hakan; Bilgili, ÖzlemThe effect of partial substitution of Ca by Zn in Bi 1.7Pb 0.3Sr 2Ca 2-x Zn x Cu 3O y at x=0.00, 0.05, 0.10, 0.15 and 0.20 levels on the electrical and structural properties was investigated in this work. The characterization of the ceramics prepared by the conventional solid-state reaction method were done by resistance-temperature measurements, XRD, SEM and density analysis. Low levels of Zn substitution of Ca caused significant changes in the properties of the ceramics. The low-T c superconducting properties were enhanced and the fraction of the low-T c (2212) phase were found to increase at x=0.15 level of Zn substitution at 830°C sintering temperature. Zero resistance was observed only in sample D with x=0.15 and the T c was determined as 92 K. The SEM micrographs and the density analysis have shown that this was the densest packed ceramic.