Chemical Engineering / Kimya Mühendisliği
Permanent URI for this collectionhttps://hdl.handle.net/11147/14
Browse
3 results
Search Results
Article Citation - WoS: 36Citation - Scopus: 39Transesterification of Sunflower Oil on Single Step Sol-Gel Made Al2o3 Supported Cao Catalysts: Effect of Basic Strength and Basicity on Turnover Frequency(Elsevier Ltd., 2012) Umdu, Emin Selahattin; Şeker, ErolThe activities of single step sol-gel made calcium oxide on alumina catalysts were studied as a function of CaO loading, methanol/oil molar ratio and the amount of the catalyst in the transesterification of sunflower oil at 50°C. Also, the turnover frequency (TOF) of the catalysts was calculated to better understand the relationship between the basicity/basic strength and the catalytic activity. From volcano curve (TOF vs. basic strength), it was found that under 50°C and methanol/oil molar ratio of 9, 60% CaO/Al 2O 3 had the highest turnover frequency, 0.028s -1, whereas 85% CaO/Al 2O 3 showed the highest biodiesel yield, ∼96.6%, but TOF obtained on it was 0.012s -1. It seemed that 60% CaO catalyst had the proper basic strength to obtain the highest TOF. © 2011 Elsevier Ltd.Article Citation - WoS: 21Citation - Scopus: 32Separation of Whey Components by Using Ceramic Composite Membranes(Elsevier Ltd., 2006) Erdem, İlker; Çiftçioğlu, Muhsin; Harsa, Hayriye ŞebnemCeramic supports were prepared from alumina powder and dip-coated with zirconia sol. The ceramic composite membranes prepared were characterized with respect to their microstructure/pore structures. The supports were 40% porous of which 87% were open pores. The average particle size of the sol particles was 35 nm. The prepared membrane has good protein lactose separation properties with a relatively high protein content (PR ∼80%) and with relatively low lactose retention (LR ∼7%). The permeate flux value was around 40 l/m2h. These results indicate the possibility of the preparation of ceramic composite membranes for separation of whey components with higher yields.Article Citation - WoS: 5Citation - Scopus: 7Alumina/Water Suspensions in the Presence of Peo-Ppo Triblock Copolymers(Elsevier Ltd., 2004) Şakar Deliormanlı, Aylin; Polat, Hürriyet; Çiftçioğlu, MuhsinThe aim of this study was to investigate the stability and dispersion behaviour of aqueous alumina suspensions in the presence of polyethylene oxide-polypropylene oxide-polyethylene oxide (PEO-PPO-PEO) type triblock copolymers. For this purpose alumina suspensions at various solids loadings were prepared using four different methods. These are: Method I: powder and water were stirred only; Method II: powder and water were stirred and ultrasonic treatment was applied; Method III: powder and water were stirred in the presence of block copolymers; Method IV: powder and water were stirred and ultrasonic treatment was applied in the presence of block copolymers. These suspensions were characterized by means of rheological measurements. Sedimentation and turbidity measurements were also conducted to support these results and to investigate the stability of these systems for longer times. Surface tension measurements were performed to investigate the adsorption behaviour of block copolymers onto alumina surface. It was found that the use of PEO-PPO-PEO type triblock copolymers improved the dispersion behaviour of aqueous alumina suspensions in the presence of ultrasonic treatment at low solids loadings. However their effect was not significant at high solids loadings and without ultrasonic treatment.