Chemical Engineering / Kimya Mühendisliği
Permanent URI for this collectionhttps://hdl.handle.net/11147/14
Browse
7 results
Search Results
Article Citation - WoS: 64Citation - Scopus: 78Utilization of Municipal Plastic and Wood Waste in Industrial Manufacturing of Wood Plastic Composites(Springer Verlag, 2020) Başalp, Dildare; Tıhmınlıoğlu, Funda; Sofuoğlu, Sait Cemil; İnal, Fikret; Sofuoğlu, AysunIn this study, Wood Plastic Composites (WPCs) were produced from post-consumer bulky wastes of recycled plastic and wood in order to minimize waste, decrease environmental effects of plastics, reserve natural resources, and support circular economy for sustainable production and consumption. Five different types of polypropylene (PP) or polyethylene (PE) based recycled plastics and wood obtained from urban household bulky wastes were used in the production of recycled WPC composites, r-WPCs. Virgin WPC (v-WPC) and r-WPC compounds were prepared with wood flour (WF) and maleic anhydride grafted compatibilizer (MAPP or MAPE) to evaluate the effect of recycled polymer type and compatibilizer on the mechanical properties. It was found that tensile strength properties of r-WPCs produced from recycled PP (r-PP) were higher than that of the r-WPCs produced from mixed polyolefins and recycled PE. r-WPCs containing anti-oxidants, UV stabilizers, and compatibilizer with different WF compositions were produced from only recycled garden fraction PP (PPFGF) to determine the optimum composition and processing temperature for pilot scale manufacturing of r-WPCs. Based on tensile, impact, flexural, and water sorption properties of r-WPC compounds with different formulations, the optimum conditions of r-WPC compounds for industrial manufacturing process were determined. Surface morphology of fractured surfaces as well as tensile, flexural and density results of r-WPC compounds revealed the enhancement effect of MAPP on interfacial adhesion in r-WPCs. r-WPC products (crates and table/chair legs) based on bulky wastes were produced using an injection molding process at industrial scale by using 30 wt% WF-filled r-WPC compound. This study demonstrated that r-WPC compounds from recycled bulky plastic and wood wastes can be used as a potential raw material in plastic as well as WPC industry, contributing to circular economy. GraphicArticle Citation - WoS: 19Citation - Scopus: 29Modeling of an Activated Sludge Process for Effluent Prediction—a Comparative Study Using Anfis and Glm Regression(Springer Verlag, 2018) Araromi, Dauda Olurotimi; Majekodunmi, Olukayode Titus; Adeniran, Jamiu Adetayo; Salawudeen, Taofeeq OlalekanIn this paper, nonlinear system identification of the activated sludge process in an industrial wastewater treatment plant was completed using adaptive neuro-fuzzy inference system (ANFIS) and generalized linear model (GLM) regression. Predictive models of the effluent chemical and 5-day biochemical oxygen demands were developed from measured past inputs and outputs. From a set of candidates, least absolute shrinkage and selection operator (LASSO), and a fuzzy brute-force search were utilized in selecting the best combination of regressors for the GLMs and ANFIS models respectively. Root mean square error (RMSE) and Pearson’s correlation coefficient (R-value) served as metrics in assessing the predicting performance of the models. Contrasted with the GLM predictions, the obtained modeling results show that the ANFIS models provide better predictions of the studied effluent variables. The results of the empirical search for the dominant regressors indicate the models have an enormous potential in the estimation of the time lag before a desired effluent quality can be realized, and preempting process disturbances. Hence, the models can be used in developing a software tool that will facilitate the effective management of the treatment operation.Article Citation - WoS: 12Citation - Scopus: 12Peg and Peg-Peptide Based Doxorubicin Delivery Systems Containing Hydrazone Bond(Springer Verlag, 2018) Balcı, Beste; Top, AybenmPEG and mPEG-peptide based drug delivery systems were prepared by conjugating doxorubicin (DOX) to these carrier molecules via hydrazone bond. The peptide, AT1, with a sequence of CG3H6G3E served as mPEG and doxorubicin attachment site. Histidines were incorporated to the sequence to improve pH responsiveness of the carrier molecule. Hydrodynamic diameters (mean sizes) of mPEG-based drug delivery system (mPEG-HYD-DOX) were measured as 9 ± 0.5 and 7 ± 0.5 nm at pH 7.4 and pH 5.0, respectively. Mean size of the aggregates of the peptide containing drug delivery system, mPEG-AT1-DOX, was determined as 12 ± 2 nm at neutral pH. At pH 5.0, on the other hand, mPEG-AT1-DOX exhibited a size distribution between 20 and 100 nm centered at about 40 nm. Comparison of % DOX release values of the drug delivery systems obtained at pH 7.4 and pH 5.0 indicated that mPEG-AT1-DOX has enhanced pH sensitivity. DOX equivalent absolute IC50 values were obtained as 0.96 ± 0.51, 21.9 ± 5.9, and 5.55 ± 0.75 μg/mL for free DOX, mPEG-HYD-DOX, and mPEG-AT1-DOX, respectively. Considering more pronounced pH sensitivity and cytotoxicity of mPEG-AT1-DOX, the use of both pH responsive functional groups and acid cleavable chemical bond between the carrier molecule and drug can be a promising approach in the design of drug delivery systems for cancer therapy.Article Citation - WoS: 23Citation - Scopus: 24Epoxidation of Propene by High-Throughput Screening Method Over Combinatorially Prepared Cu Catalysts Supported on High and Low Surface Area Silica(Springer Verlag, 2012) Düzenli, Derya; Şeker, Erol; Senkan, Selim; Önal, IşıkGas phase epoxidation of propene using molecular oxygen was studied by use of a high-throughput testing technique. A large number of catalysts including promoted and un-promoted Cu were synthesized in a much faster combinatorial fashion using a sol-gel method. Metal catalysts supported on high and low surface area silica were tested and ranked in a high-throughput activity and selectivity testing apparatus at different experimental conditions such as reaction temperature and reactant gas ratio. The amount of Cu loading and the addition of alkali promoters such as K and Li resulted in different tendencies in consumption rate for both silica materials. The maximum PO production rate was obtained as 25.82 μmol/g/ cat./min (2.90 % conv. and 20.49 % selectivity) for 3 % Cu-2.25 % K catalyst supported on high surface area silica. There was no noticeable difference in structural and chemical properties of catalysts after modification with K when examined by XRD and TEM; however, the overall activation energy of un-modified catalysts (92 kJ/mol) decreased to 71 kJ/mol for K-modified catalyst. There was negligible difference between the activation energies calculated for PO production (75 vs. 77 kJ/mol).Article Citation - WoS: 10Citation - Scopus: 11The Effects of Sb Substitution on Structural Properties in Yba 2cu 3o 7 Superconductors(Springer Verlag, 2011) Akyüz, Gönül B.; Kocabaş, Kemal; Yıldız, Aylin; Özyüzer, Lütfi; Çiftçioglu, MuhsinIn this study, the effects of partial Sb 3+ ion substitutions for the Y sites and the Cu sites on the superconducting properties of YBa 2Cu 3O y (Y123) ceramic superconductors were investigated. The samples were prepared by the conventional solid-state reaction method and the properties of the samples were investigated by means of X-ray diffraction, AC magnetic susceptibility measurements, scanning electron microscope, and energy dispersive X-ray analysis. The critical temperatures were determined to be in the range of 80-92 K for both Systems I and II. It was found that Sb-addition leads to the formation of the non-superconducting YBa 2SbO 6 phase, which has a negative effect on the critical temperature, since the highest critical temperature was measured for pure Y123. However, the increasing substitution level has a negligible effect on the X-ray diffraction analysis peak intensities of the superconducting phases. In addition, SEM images showed that Sb substitution decreases the grain size and modifies the microstructure development, which makes the samples denser.Article Citation - WoS: 17Citation - Scopus: 19Effect of Compaction Pressure on Structural and Superconducting Properties of Bi-2223 Superconductors(Springer Verlag, 2010) Kocabaş, Kemal; Gökçe, Melis; Çiftçioğlu, Muhsin; Bilgili, ÖzlemIn this work, effects of compaction pressure on the structural and superconducting properties of BSCCO ceramic superconductors were investigated. The study was carried out on two systems which were, System I: Bi 1.7Pb 0.3Sr 2Ca 2Cu 3O y and System II: Bi 1.6Pb 0.3Ag 0.1Sr 2Ca 2Cu 3O y, respectively. Ceramic powders were prepared by conventional solid-state reaction method and sintered at 850°C after compaction at five different pressures in the 150-750 MPa range. Critical temperatures of samples were determined by resistivity-temperature determinations made by four-point probe method in liquid nitrogen conditions. XRD analysis was conducted by powder X-ray diffraction method. Morphology of the grains present in the samples were determined by using scanning electron microscope (SEM) photographs at 2 K× and 2.5 K× magnifications for System I and System II, respectively. Sintered densities of the superconducting ceramics were measured by Archimedes water displacement method and unit cell parameters were additionally obtained from XRD data. T c values for System I was determined to be in the 109-115 K with sample D having the highest T c of 115 K while T c varied in the 104-109 K range and sample B had the highest T c value of 109 K for System II. The transition width, which is a sign of the purity of the samples, was determined to be narrow for both systems. The data obtained from X-ray diffraction measurements have shown that 2223 high-T c phase was dominant in both systems. The determination of the optimum pellet compaction pressure for BSCCO ceramic superconductors was the main purpose of this work. The results of this work indicated that compaction at around 450 MPa improves the superconducting and structural properties of the BSCCO ceramic superconductors. © 2009 Springer Science+Business Media, LLC.Article Citation - WoS: 12Citation - Scopus: 12The Effect of Zn Substitution of Ca in Bipbsrcacuo Superconductors Sintered at 830°c(Springer Verlag, 2009) Kocabaş, Kemal; Şakiroğlu, Serpil; Çiftçioğlu, Muhsin; Ercan, İsmail; Epik, Hakan; Bilgili, ÖzlemThe effect of partial substitution of Ca by Zn in Bi 1.7Pb 0.3Sr 2Ca 2-x Zn x Cu 3O y at x=0.00, 0.05, 0.10, 0.15 and 0.20 levels on the electrical and structural properties was investigated in this work. The characterization of the ceramics prepared by the conventional solid-state reaction method were done by resistance-temperature measurements, XRD, SEM and density analysis. Low levels of Zn substitution of Ca caused significant changes in the properties of the ceramics. The low-T c superconducting properties were enhanced and the fraction of the low-T c (2212) phase were found to increase at x=0.15 level of Zn substitution at 830°C sintering temperature. Zero resistance was observed only in sample D with x=0.15 and the T c was determined as 92 K. The SEM micrographs and the density analysis have shown that this was the densest packed ceramic.