Chemical Engineering / Kimya Mühendisliği
Permanent URI for this collectionhttps://hdl.handle.net/11147/14
Browse
4 results
Search Results
Article Citation - WoS: 10Citation - Scopus: 10Morphology, Order, Light Transmittance, and Water Vapor Permeability of Aluminum-Coated Polypropylene Zeolite Composite Films(John Wiley and Sons Inc., 2011) Balköse, Devrim; Oğuz, Kaan; Özyüzer, Lütfi; Tarı, Süleyman; Arkış, Esen; Özmıhçı Ömürlü, FilizIn this study, the polypropylene-zeolite composite films having 2-6 wt % natural zeolite were coated with a thin film of aluminum (Al) by magnetron sputtering, and the contribution of the Al coating on film properties was investigated. The samples were characterized by EDX, X-ray diffraction, SEM, AFM, UV-visible spectroscopy, and water vapor permeation analyses. The surface of the films coated with a smooth Al film having 98-131 nm thickness. EDX revealed that Al percentage on the surface appeared to be as 8-10 wt % indicating contribution of polymer surface under Al film to analysis. XRD analysis showed that the grain size of Al at the surface was 22-29 nm. The surface roughness increased after Al-coating process. The transmission of coated films was very low for both UV and visible regions of the light spectrum. Permeation analysis indicated that water vapor permeation was lower for Al-coated material.Article Citation - WoS: 13Citation - Scopus: 18Effect of Corn-Zein Coating on the Mechanical Properties of Polypropylene Packaging Films(John Wiley and Sons Inc., 2011) Tıhmınlıoğlu, Funda; Atik, İsa Doğan; Özen, BanuIn this study, a novel film structure of corn zein coated on polypropylene (PP) synthetic films for food packaging applications was developed, and the mechanical properties of the resulting coated film, as affected by the coating formulation, were investigated. Composite structures of PP films coated with corn zein were obtained through a simple solvent casting method. Different amounts of corn zein (5 and 15%) were dissolved in 70 and 95% aqueous ethanol solution at 50 C. Solutions of corn zein plasticized with poly(ethylene glycol) and glycerol (GLY) at various levels (20 and 50%) were applied on corona-discharge-treated PP. A statistical analysis based on full factorial design was performed to examine the influence of the coating formulation on the final properties of the corn-zein-coated PP films. A significant (p < 0.05) improvement in the coated film’s mechanical properties was observed compared to those of the uncoated PP. The effect of the plasticization of the coating solutions was also quite significant. In general, GLY provided better improvements in the mechanical properties of the corn-zein-coated PP films. The statistical analysis of the results showed that the corn-zein and plasticizer concentrations and plasticizer type used in the coating formulations were more effective parameters and had significant effects on the mechanical behavior of the coated PP films. In conclusion, corn-zein coatings could have potential as alternatives to conventional synthetic polymers used in composite multilayer structures for food packaging applications.Article Citation - WoS: 30Citation - Scopus: 31Water and Water Vapor Sorption Studies in Polypropylene-Zeolite Composites(Wiley, 2003) Pehlivan, Hilal; Özmıhçı, Filiz; Tıhmınlıoğlu, Funda; Balköse, Devrim; Ülkü, SemraWater and water vapor sorption to porous polypropylene-zeolite composites prepared by hot pressing have been studied as a function of zeolite loading. This work presents the first report on the effect of the zeolite as a filler on the water-sorption properties of PP composites. Water swelling experiments were conducted at 25°C using pure PP and PP-zeolite films samples having different zeolite loadings (6-40 wt %). Because PP is a hydrophobic polymer, it does not sorp any water, but the composites having 10, 20, 30, and 40% zeolites have sorbed 0.63, 1.00, 1.72 and 3.74% water, respectively. The zeolite itself at the same conditions sorbed 24.5% water. As the filler loading in the composites increased, equilibrium uptake values increased also. On the other hand, water vapor sorption and kinetics has been studied using a Cahn 2000 gravimetric sorption system. Within in the range of 0.35-0.95% water vapor was adsorbed by the composites containing 10-40 wt % zeolites. Experimental effective water vapor diffusivities of the composite films was about one order of magnitude higher (10-fold) than the experimental water diffusion coefficient in composites. The transport of water in composites was slower than that in the liquid water due to the longer diffusion pathway and adsorption on the surface of the composites. Although the liquid water may fill all the voids in the composite, water vapor is adsorbed on the surface of the zeolite only.Article Citation - WoS: 42Citation - Scopus: 42Natural Zeolite Polypropylene Composite Film Preparation and Characterization(John Wiley and Sons Inc., 2001) Özmıhçı, Filiz; Balköse, Devrim; Ülkü, SemraIn this research, the preparation and characterization of polypropylene (PP) and natural zeolite composites were studied. Natural zeolite mined in Gördes, Turkey was used as an alternative filler to CaCO3. Films were prepared by the extrusion of PP, and surface-modified zeolite was made by polyethylene glycol 4000 with 2-4% zeolite. Zeolite-filled composites had densities between 0.73 and 0.83 g/cm3 and had void fractions of 0.07-0.20. Although the permeability of water vapour through 2% zeolite-filled composites was very small, 4% zeolite-filled films had very high permeabilities. The yield stresses of 2-4% zeolite-containing films were around 26-27 N/mm2 and were lower than that of PP, which indicated no adhesion between PP and zeolite. The effect of zeolite on the thermal degradation behaviour in air and in a N2 atmosphere was also studied. In air, zeolites did not cause the oxidation of PP. In a N2 atmosphere, although the start of the thermal degradation of PP was retarded by zeolite, composites degraded at a faster rate than PP once the degradation started. At a processing temperature of 200°C, zeolites had no effect on the degradation of PP.