Chemical Engineering / Kimya Mühendisliği
Permanent URI for this collectionhttps://hdl.handle.net/11147/14
Browse
2 results
Search Results
Now showing 1 - 2 of 2
Article Citation - WoS: 54Citation - Scopus: 62A Positively Charged Loose Nanofiltration Membrane Fabricated Through Complexing of Alginate and Polyethyleneimine With Metal Ions on the Polyamideimide Support for Dye Desalination(Elsevier, 2021) Metecan, Ayşe; Cihanoğlu, Aydın; Alsoy Altınkaya, SacideNowadays, loose nanofiltration (NF) membranes are preferred for dye desalination to achieve high dye/salt selectivity and enable filtration at low operating pressure. However, current fabrication techniques require rigorous reaction conditions and long preparation times. Herein, we used the chelating ability of the polyethyleneimine (PEI) and alginate with the metal ions to fabricate loose NF membranes via a facile approach. The positively charged polyamide imide (PAI)/PEI support was used to build the assembly. Direct attachment of Zn or Fe ions to the PEI chains did not result in a stable complex in the presence of a high salt concentration (1000 ppm NaCl). On the other hand, alginate coated on the support allowed building permanent assemblies after crosslinked with Fe3+ and Zn2+ transition metal ions. The PAI/PEI-Alg-Fe3+ membrane exhibited the highest permeability, excellent antifouling behaviour upon exposure to synthetic textile wastewater, and maintained long-term stability under static and dynamic conditions. Also, the same membrane rejected dyes and coloured substances in real wastewater sample during 72 h continuous filtration. With alginate metal complex formation on a suitable support, a scalable loose NF membrane was manufactured, demonstrating improved throughput value compared to current NF membranes.Article Citation - WoS: 34Citation - Scopus: 35Development of High Flux Nanofiltration Membranes Through Single Bilayer Polyethyleneimine/Alginate Deposition(Elsevier Ltd., 2019) Tekinalp, Önder; Alsoy Altınkaya, SacideThe aim of this study is to prepare high flux, stable, antifouling nanofiltration membranes through single bilayer polyelectrolyte deposition. To this end, a tight ultrafiltration support membrane was prepared from a polysulfone/sulfonated polyethersulfone blend. Deposition of a polyethyleneimine and alginate pair on this support has reduced the molecular weight cut off from 6 kDa to below 1 kDa. The pure water permeability and polyethylene glycol 1000 rejection of the coated membrane were found to be 15.5 ± 0.3 L/m2·h·bar and 90 ± 0.6%, respectively, by setting the deposition pH for each layer to 8 and the ionic strengths to 0.5 M and 0 M. This membrane has exhibited significantly higher permeability than commercial membranes with the same molecular weight cut off, retaining 98% of the initial flux during 15 h filtration of bovine serum albumine. In addition, the membrane has been able to completely remove anionic dyes from aqueous solution by showing 99.9% retentions to Reactive red 141, Brilliant blue G and Congo red with a 2 bar transmembrane pressure. High flux and membrane stability in acidic and salty environments have been achieved when deposition conditions favor high adsorption levels for the first layer and strong ionic cross-linking between the carboxyl group on the alginate and the amine groups on the polyethyleneimine