Materials Science and Engineering / Malzeme Bilimi ve Mühendisliği
Permanent URI for this collectionhttps://hdl.handle.net/11147/4719
Browse
4 results
Search Results
Article Citation - WoS: 22Citation - Scopus: 25Effect of Solution Heat Treatment on the Microstructure and Crystallographic Texture of In939 Fabricated by Powder Bed Fusion-Laser Beam(Elsevier, 2023) Doğu, Merve Nur; Özer, Seren; Yalçın, Mustafa Alp; Davut, Kemal; Bilgin, Guney Mert; Obeidi, Muhannad Ahmed; Brodin, Hakan; Gu, Hengfeng; Brabazon, DermotThe effect of various solution heat treatment temperatures (i.e., 1120, 1160, 1200 and 1240 & DEG;C) on the microstructure, grain morphology and crystallographic texture of IN939 fabricated by powder bed fusion-laser beam (PBF-LB) was investigated. Microstructural analyses showed that the high-temperature gradient and rapid solidification of the PBF-LB processing caused different resulting microstructures compared to conventionally pro-duced counterparts. The melt pool morphologies and laser scanning paths were examined in the as-fabricated samples in the XZ-and XY-planes, respectively. After the application of solution heat treatment at 1120 & DEG;C, the as-fabricated PBF-LB initial microstructure was still apparent. For solution heat treatments of 1200 & DEG;C and above, the melt pool and scanning path morphologies disappeared and converted into a mixture of columnar grains in the XZ-plane and equiaxed grains in the XY-plane. On the other hand, large equiaxed grains were observed when the samples were solutionized at 1240 & DEG;C. Additionally, g' phase precipitated within the matrix after all solution heat treatment conditions, which led to increase in the microhardness values. According to electron backscatter diffraction (EBSD) analyses, both as-fabricated and solution heat-treated samples had intense texture with {001} plane normal parallel to the building direction. The first recrystallized grains began to appear when the samples were subjected to the solution heat treatment at 1160 & DEG;C and the fraction of the recrystallized grains increased with increasing temperature, as supported by kernel average misorientation (KAM) and grain spread orientation (GOS) analyses.& COPY; 2023 The Author(s). Published by Elsevier B.V. This is an open access article under the CC BY license (http://creativecommons.org/licenses/by/4.0/).Article Citation - WoS: 29Citation - Scopus: 31Effect of Heat Input on Haz Softening in Fiber Laser Welding of 22mnb5 Steel(Elsevier, 2023) Tuncel, Oğuz; Aydın, Hakan; Davut, KemalThis study investigates the effects of heat input on the heat-affected zone (HAZ) softening in fiber laser welding of quenched 1.1 mm thick 22MnB5 steel. Laser power (1500-2500 W) and welding speed (40-120 mm/s) parameters are considered as the input process variables. Depending on the input parameters, the applied heat input varied between 12.5 and 62.5 J/mm. The results indicate that a minimum heat input of 50 J/mm is required for full weld penetration. Microhardness findings revealed that the drop in hardness in the HAZ region relative to the base material (BM) reached 39% due to grain coarsening caused by an increase in heat input under the welding conditions. Grain coarsening (prior austenite grains) is also detected in SEM analysis. In addition, grain coarsening at high heat input was also determined quantitatively in EBSD analyses. The proportion of 8.91 mu m grain size in the sample with high heat input is 4.2%, while it is 1.2% in the sample with low heat input. When the heat input increased from 12.5 to 62.5 J/mm, the width of the softened zone with the lowest hardnesses in the HAZ grew from 0.2 mm to 2.2 mm.Article Citation - WoS: 3Citation - Scopus: 3Nondestructive Microstructural Characterization of Austempered Ductile Iron(Walter de Gruyter GmbH, 2023) Tüzün, Mert Yağız; Yalçın, Mustafa Alp; Davut, Kemal; Kılıçlı, VolkanAustempered ductile iron (ADI) has been preferred in a wide range of applications due its unique combination of high strength, good ductility, wear resistance and fracture toughness together with lower cost and lower density compared to steels. Magnetic Barkhausen noise (MBN) measurement offers a better alternative to traditional characterization techniques by being fast and non-destructive. A simple linear regression using only one single independent variable cannot correlate the MBN with the microstructure of ADI, since its microstructure is multi component. Multiple linear regression analysis (MLRA) was used to build a model that uses the characteristic features of microstructural constituents as input parameters to predict the MBN. For that purpose, Cu-Ni-Mo alloyed ductile iron samples austempered between 325 and 400 degrees C and for 45-180 min duration were used. The results show that MBN is most sensitive to the size and shape of acicular ferrite and retained austenite. Moreover, MBN is almost insensitive to the size, morphology and volume fraction of graphite particles. This indicates that retained austenite pins the domain walls more effectively than the graphite particles. Considering the results MLRA, MBN technique can be used to characterize the ausferritic microstructure of ADI.Article Citation - WoS: 45Citation - Scopus: 48Recrystallization and Grain Growth Kinetics of In718 Manufactured by Laser Powder Bed Fusion(Elsevier, 2022) Doğu, Merve Nur; Davut, Kemal; Obeidi, Muhannad Ahmed; Yalçın, Mustafa Alp; Gu, Hengfeng; Low, Thaddeus Song En; Ginn, Jon; Brabazon, DermotThe recrystallization and grain growth behaviour of IN718 alloy additively manufactured by laser powder bed fusion (L-PBF) is presented herein. The effects of three different temperatures (1050, 1150 and 1250 °C) and holding times (15, 45 and 90 min) were investigated. The texture evolution of the samples was recorded via electron backscatter diffraction (EBSD). The as-built sample is composed of bowl-shaped melt pools, a chessboard-like grain pattern and has a cube texture {100}<001>. Recrystallized grains were observed in the samples treated at 1150 °C for 15 min, as well as the samples treated for longer periods and at higher temperatures. Recrystallization was observed to start from high dislocation density regions, including the overlapping melt pools and the borders of the chessboard-like pattern. The initial cube texture transforms into a first-generation cube-twin texture {122}<212> via a twinning-assisted recrystallization mechanism. Then, those recrystallization nuclei sweep through the high defect density matrix; during which almost no new twins are formed. The samples treated at 1250 °C are almost completely recrystallized, which forms a weaker cube texture and a stronger P-orientation {011}<112>. However, the growth of recrystallized grains is very limited due to the presence of non-coherent precipitates.