Materials Science and Engineering / Malzeme Bilimi ve Mühendisliği
Permanent URI for this collectionhttps://hdl.handle.net/11147/4719
Browse
3 results
Search Results
Now showing 1 - 3 of 3
Article Citation - WoS: 8Citation - Scopus: 8Crystallization and Additional Oxide Interlayers Improve the Tribocorrosion Resistance of Tio2 Nanotubular Surfaces Formed on Ti6al4v(Elsevier, 2023) Çaha, İhsan; Türü, İrem Cemre; Erdoğan, Ece; Pinto, Ana Maria Pires; Cansever, Nurhan; Deepak, Francis Leonard; Toptan, Fatih; Alves, Alexandra C.TiO2-based nanotubular surfaces have promising properties for various industrial applications, such as solar cells, fuel cells, photocatalysis, energy storage, gas sensors, and biomedical applications. However, they have very limited use in real applications, and one of the major limiting factors is the weak adhesion of nanotubular surfaces to the substrate. In this study, nanotubular surfaces are formed on Ti6Al4V alloy by anodic treatment followed by a heat treatment at 500 °C for 3 h under an open atmosphere. Microstructural investigations revealed self-organized nanotubes grown on both ? and ? phases. High-resolution TEM/STEM analysis showed crystallization of the nanotubular layer and formation of additional oxide interlayers resulting in a drastic improvement in tribocorrosion resistance. These findings indicated that a simple heat treatment can significantly alter the properties of nanotubular layers and can widen their usage mainly for load-bearing implant applications in corrosive environments. © 2023 Elsevier B.V.Article Citation - WoS: 10Citation - Scopus: 10Influence of Calcium Acetate Concentration in Electrolyte on Tribocorrosion Behaviour of Mao Treated Titanium(MDPI Multidisciplinary Digital Publishing Institute, 2021) Sousa, Luis; Mendes, Ana Rita; Pinto, Ana Maria Pires; Toptan, Fatih; Alves, Alexandra CruzTi-based materials are widely used for dental and orthopaedic implant applications due to their adequate mechanical properties, corrosion behaviour and biocompatibility. However, these materials are biologically inert and display poor wear resistance. In one of the most studied processes that aims to overcome these drawbacks, Ti surfaces are often covered by anodic oxide films with the incorporation of bioactive agents such as Ca and P. Although there are several works on the tribocorrosion behaviour of MAO-treated Ti surfaces, the influence of electrolyte composition on the corrosion kinetics under sliding is yet to be fully understood. In the present work, anodic oxide films were produced on cp-Ti surfaces with different calcium acetate concentrations in the electrolyte. Tribocorrosion behaviour was investigated by reciprocating sliding tests performed in 8 g/L NaCl solution at body temperature, under potentiostatic conditions. The results showed that higher concentrations of calcium acetate had a detrimental effect on tribocorrosion kinetics, however, they resulted in less mechanical damage due to alterations in the topography and structure of the MAO layer.Article Citation - WoS: 5Citation - Scopus: 6Degradation Behaviour of Ti-12nb Alloy Coated With Zno/Tin Double Layer(Elsevier, 2021) Çaha, İhsan; Alves, A. C.; Affonco, L. J.; da Silva, J. H. D.; Rodrigues, I. R.; Grandini, C. R.; Rocha, L. A.; Pinto, Ana Maria Pires; Lisboa Filho, P. N.; Toptan, FatihTi and its alloys have attracted attention for biomedical applications, but their low tribocorrosion resistance, lack of bioactivity and antimicrobial properties are still major clinical concerns. In this study a ZnO coating, intended to act as an antibacterial agent, was deposited on a Ti-12Nb alloy, which was previously coated with a TiN hard coating, for improving tribocormsion resistance. The idea behind is the proof-of -concept that ZnO is able to provide interesting tribological properties to the surface, thus inspiring new ZnO-containing surfaces that can combine antimicrobial properties and tribocormsion resistance. Thus, the corrosion behaviour was studied by open circuit potential, electrochemical impedance spectroscopy, and potentiodynamic polarization tests in phosphate buffered solution at body temperature. The tribocormsion behaviour was carried out at open circuit potential under 0.5 N of normal load, 1 Hz frequency, during 3600 s sliding in phosphate buffered solution at body temperature. The results indicated that duplex coating sample showed better corrosion resistance and drastically better tribocorrosion resistance compared to uncoated and single TiN coating samples.