Chemistry / Kimya
Permanent URI for this collectionhttps://hdl.handle.net/11147/4072
Browse
3 results
Search Results
Conference Object Citation - Scopus: 2Utilization of Near Ir Absorbing Gold Nanocolloids by Green Synthesis(Trans Tech Publications, 2018) Elveren, Beste; Yıldız, Ümit Hakan; Arslan Yıldız, AhuThe rapid developments in nanoscience, and its applications on biomedical areas have a large impact on drug delivery, tissue engineering, sensing, and diagnosis. Gold is widely investigated nanomaterial for the last couple of decades, since it has unique surface properties and very low toxicity to biological environment. In this work, we present a novel synthesis of gold nanoparticles (GNPs) exhibiting both visible and near-IR absorbance without agglomeration. The surface of GNPs were analyzed by routine methods and the binding kinetics were investigated by Surface Plasmon Resonance (SPR) Spectroscopy. The unique optical properties of near-IR asorbing GNP colloids hold promise for biological applications.Conference Object Citation - Scopus: 2Fabrication of Polymer Nanofiber-Conducting Polymer Fabric and Noncontact Motion Sensing Platform(Trans Tech Publications, 2018) Mutlu, Mustafa Umut; Akın, Osman; Demir, Mustafa Muammer; Yıldız, Ümit HakanConductive polymer-electrospun polymer nanofiber network was combined to host iron oxide nanoparticles providing micrometer thick sensing interface. The sensor has fabricated as freestanding fabric exhibiting 10 to 100 KOhm base resistivity upon bias applied. The moving object has been sensed through the electrostatic interactions between fibers and object. The sensing range has been found to be 1-5 cm above the surface of fabric. By the controlled combination of conductive polymers electrospun polymer nanofibers effective device miniaturization has been provided without loss of performance. The noncontact motion sensor platform has unique flexibility and light weight holding a potential for wearable sensor technology.Conference Object Citation - WoS: 2Citation - Scopus: 2Effects of Mechanical Treatment on the Formation of Α-Al 2o3 From Gibbsite(Trans Tech Publications, 2004) Şakar Deliormanlı, Aylin; Çiftçioğlu, Muhsin; Polat, HürriyetIn this study preparation of fine alpha alumina powders derived from Bayer gibbsite was studied. Preparation of the alumina powders was performed by decomposition of the gibbsite into transition alumina phase followed by controlled transformation to the alpha phase. Gibbsite was thermally treated at 350°C and 900°C to obtain a transition form of alumina. The purpose of the heat treatment at 350°C was to increase the surface area of the gibbsite particles and obtain a loosely packed structure that may reduce the size of the rather coarse precursor gibbsite during the grinding step. Mechanical treatment (by using ultrasonic forces and impact forces) was utilized to increase the transformation rate to the alpha alumina in the transition phase matrix and influence the nucleation and growth rate of the solid -solid phase transformation. These powders were calcined at 1100, 1200 and 1450°C for 1 to 8 hours. Results indicated that transformation to the alpha phase was accomplished in the powders preheated at 900°C, ultrasonically treated or ground, and then calcined at 1200°C for 2 to 8 hours or at 1450°C for 2 hours. Ultrasonic treatment accelerated the transformation rate to the alpha phase at 1100°C in 2 hours. Powders that were calcined at 1100 to 1200°C for 1 hour had a significant kappa content together with the alpha phase. Additionally the powder prepared without mechanical treatment and calcined at 1100°C was mainly in the kappa phase.