    Fabrication of 3d Printed Poly(lactic Acid) Strut and Wet-Electrospun Cellulose Nano Fiber Reinforced Chitosan-Collagen Hydrogel Composite Scaffolds for Meniscus Tissue Engineering
    (SAGE Publications, 2022) Güneş, Oylum Çolpankan; Kara, Aylin; Baysan, Gizem; Hüsemoğlu, Reşit Buğra; Akokay, Pınar; Ziylan Albayrak, Aylin; Ergür, Bekir Uğur; Havitçioğlu, Hasan
    The main goal of the study was to produce chitosan-collagen hydrogel composite scaffolds consisting of 3D printed poly(lactic acid) (PLA) strut and nanofibrous cellulose for meniscus cartilage tissue engineering. For this purpose, first PLA strut containing microchannels was incorporated into cellulose nanofibers and then they were embedded into chitosan-collagen matrix to obtain micro- and nano-sized topographical features for better cellular activities as well as mechanical properties. All the hydrogel composite scaffolds produced by using three different concentrations of genipin (0.1, 0.3, and 0.5%) had an interconnected microporous structure with a swelling ratio of about 400% and water content values between 77 and 83% which is similar to native cartilage extracellular matrix. The compressive strength of all the hydrogel composite scaffolds was found to be similar (∼32 kPa) and suitable for cartilage tissue engineering applications. Besides, the hydrogel composite scaffold comprising 0.3% (w/v) genipin had the highest tan δ value (0.044) at a frequency of 1 Hz which is around the walking frequency of a person. According to the in vitro analysis, this hydrogel composite scaffold did not show any cytotoxic effect on the rabbit mesenchymal stem cells and enabled cells to attach, proliferate and also migrate through the inner area of the scaffold. In conclusion, the produced hydrogel composite scaffold holds great promise for meniscus tissue engineering.
  • Article
    Citation - WoS: 51
    Citation - Scopus: 58
    3d Printed Gelatin/Decellularized Bone Composite Scaffolds for Bone Tissue Engineering: Fabrication, Characterization and Cytocompatibility Study
    (Elsevier, 2022) Kara, Aylin; Distler, Thomas; Polley, Christian; Schneidereit, Dominik; Seitz, Hermann; Friedrich, Oliver; Tıhmınlıoğlu, Funda; Boccaccini, Aldo R
    Three-dimensional (3D) printing technology enables the design of personalized scaffolds with tunable pore size and composition. Combining decellularization and 3D printing techniques provides the opportunity to fabricate scaffolds with high potential to mimic native tissue. The aim of this study is to produce novel decellularized bone extracellular matrix (dbECM)-reinforced composite-scaffold that can be used as a biomaterial for bone tissue engineering. Decellularized bone particles (dbPTs, ∼100 ​μm diameter) were obtained from rabbit femur and used as a reinforcement agent by mixing with gelatin (GEL) in different concentrations. 3D scaffolds were fabricated by using an extrusion-based bioprinter and crosslinking with microbial transglutaminase (mTG) enzyme, followed by freeze-drying to obtain porous structures. Fabricated 3D scaffolds were characterized morphologically, mechanically, and chemically. Furthermore, MC3T3-E1 mouse pre-osteoblast cells were seeded on the dbPTs reinforced GEL scaffolds (GEL/dbPTs) and cultured for 21 days to assess cytocompatibility and cell attachment. We demonstrate the 3D-printability of dbPTs-reinforced GEL hydrogels and the achievement of homogenous distribution of the dbPTs in the whole scaffold structure, as well as bioactivity and cytocompatibility of GEL/dbPTs scaffolds. It was shown that Young's modulus and degradation rate of scaffolds were enhanced with increasing dbPTs content. Multiphoton microscopy imaging displayed the interaction of cells with dbPTs, indicating attachment and proliferation of cells around the particles as well as into the GEL-particle hydrogels. Our results demonstrate that GEL/dbPTs hydrogel formulations have potential for bone tissue engineering.
  • Article
    Citation - WoS: 12
    Citation - Scopus: 17
    Fish Scale/Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) Nanofibrous Composite Scaffolds for Bone Regeneration
    (SAGE Publications, 2020) Kara, Aylin; Güneş, Oylum C.; Albayrak, Aylin Z.; Bilici, Gökçen; Erbil, Güven; Havitcioğlu, Hasan
    The aim of this study was to produce three-dimensional, nanofibrous fish scale/poly(3-hydroxybutyrate-co-3-hydroxyvalerate) composite scaffolds as bone filling materials. This is the first report wherein fish scales were used within a nanofibrous matrix for bone regeneration. Composite scaffolds with a cotton wool-like structure (fiber diameter: 560 +/- 64 nm; porosity: 82%) were obtained by incorporating chopped fish scales into wet-electrospun poly(3-hydroxybutyrate-co-3-hydroxyvalerate) nanofibers and freeze-drying. The addition of the fish scales improved the mechanical properties, biomineralization tendency, cell viability, alkaline phosphatase activity, and type I collagen production. Consequently, produced composite scaffolds would be regarded to have the therapeutic capacity in bone tissue damages.