PubMed İndeksli Yayınlar Koleksiyonu / PubMed Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7645
Browse
2 results
Search Results
Article Citation - WoS: 22Citation - Scopus: 25Null Extinction of Ceria@silica Hybrid Particles: Transparent Polystyrene Composites(American Chemical Society, 2015) İncel, Anıl; Güner, Tuğrul; Parlak, Onur; Demir, Mustafa MustafaScattering of light in optical materials, particularly in composites based on transparent polymer and inorganic pigment nanoparticles, is a chronic problem. It might originate mainly from light scattering because of a refractive index mismatch between the particles and transparent polymer matrix. Thus, the intensity of light is rapidly diminished and optical transparency is reduced. Refractive index matching between the pigment core and the surrounding transparent matrix using a secondary component at the interface (shell) has recently appeared as a promising approach to alter light scattering. Here, CeO2 (ceria) nanoparticles with a diameter of 25 nm are coated with a SiO2 (silica) shell with various thicknesses in a range of 6.5-67.5 nm using the Stöber method. When the hybrid core-shell particles are dispersed into transparent polystyrene (PS), the transmission of the freestanding PS composite films increases over both the ultraviolet (UV) and visible region as the shell thickness increases particularly at 37.5 nm. The increase of transmission can be attributed to the reduction in the scattering coefficient of the hybrid particles. On the other hand, the particles in tetrahydrofuran (THF) absorb over UV and the intensity of absorption shows a systematic decrease as the shell thickness increases. Thus, the silica shell suppresses not only the scattering coefficient but also the molar absorptivity of the core ceria particles. The experimental results regarding the target shell thickness to develop low extinction (scattering + absorption) composites show a qualitative agreement with the predictions of Effective Medium Theory.Article Citation - WoS: 11Citation - Scopus: 11Effect of Alkali Metal Hydroxides on the Morphological Development and Optical Properties of Ceria Nanocubes Under Hydrothermal Conditions(American Scientific Publishers, 2011) Kepenekçi, Özlem; Eanes, Mehtap; Demir, Mustafa MustafaNanocrystalline cerium(IV) oxide (CeO2, ceriaceria) particles were produced via the hydrothermal treatment of cerium nitrate hexahydrate with various alkali metal hydroxides (MOH: M = Li, Na, K). Experimental conditions such as [MOH], reaction temperature, and reaction time were studied. Particle morphology as well as size of crystallites was precisely controlled by choice of experimental conditions. While rod-shaped particles were obtained at 120 C, well-defined nanocubes were formed at higher temperatures regardless of the choice of MOH. Examination of particle growth kinetics, in the final stages of crystallization, showed that particle growth rate is controlled by two different mechanisms. Grain boundary diffusion controls the particle growth in the presence of NaOH with an activation energy of 113.8 kj/mol and surface diffusion for LiOH ad KOH with the activation energy of 43.0–150.9 kj/mol, respectively. In addition, the particles exhibit strong violet and blue emissions at 400 nm and 370 nm. The former emission originates from excitation of a wide band gap of CeO2. The latter one is attributed to the trivalency of the cerium ion and appears to be sensitive to all the experimental conditions studied. Both extending reaction time and increasing temperature reduce the intensity of the 370 nm emission and increase the intensity of the 400 nm emission.