PubMed İndeksli Yayınlar Koleksiyonu / PubMed Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7645
Browse
3 results
Search Results
Article Citation - WoS: 25Citation - Scopus: 30Fabrication of 3d Printed Poly(lactic Acid) Strut and Wet-Electrospun Cellulose Nano Fiber Reinforced Chitosan-Collagen Hydrogel Composite Scaffolds for Meniscus Tissue Engineering(SAGE Publications, 2022) Güneş, Oylum Çolpankan; Kara, Aylin; Baysan, Gizem; Hüsemoğlu, Reşit Buğra; Akokay, Pınar; Ziylan Albayrak, Aylin; Ergür, Bekir Uğur; Havitçioğlu, HasanThe main goal of the study was to produce chitosan-collagen hydrogel composite scaffolds consisting of 3D printed poly(lactic acid) (PLA) strut and nanofibrous cellulose for meniscus cartilage tissue engineering. For this purpose, first PLA strut containing microchannels was incorporated into cellulose nanofibers and then they were embedded into chitosan-collagen matrix to obtain micro- and nano-sized topographical features for better cellular activities as well as mechanical properties. All the hydrogel composite scaffolds produced by using three different concentrations of genipin (0.1, 0.3, and 0.5%) had an interconnected microporous structure with a swelling ratio of about 400% and water content values between 77 and 83% which is similar to native cartilage extracellular matrix. The compressive strength of all the hydrogel composite scaffolds was found to be similar (∼32 kPa) and suitable for cartilage tissue engineering applications. Besides, the hydrogel composite scaffold comprising 0.3% (w/v) genipin had the highest tan δ value (0.044) at a frequency of 1 Hz which is around the walking frequency of a person. According to the in vitro analysis, this hydrogel composite scaffold did not show any cytotoxic effect on the rabbit mesenchymal stem cells and enabled cells to attach, proliferate and also migrate through the inner area of the scaffold. In conclusion, the produced hydrogel composite scaffold holds great promise for meniscus tissue engineering.Article Citation - WoS: 1Citation - Scopus: 1Fabrication and in Vitro Evaluation of Thermally Cross-Linked Gelatin Nanofibers for Drug Delivery Applications(Taylor & Francis, 2022) Mete, Derya; Göktaş, Gözde; Şanlı Mohamed, GülşahIn this study, four different nanofibers consisting of gelatin (Gel), doxorubicin (DOX) with gel (DOX@Gel), a composite of gel with poly(ethylene glycol) (PEGylated-gel), and DOX@PEGylated-gel were fabricated. Subsequently, the nanofibers were thermally cross-linked in order to offer a stable and biocompatible alternative for the biological applications of nanofibers such as drug delivery and tissue engineering. Nanofibers were characterized by scanning electron microscopy, Fourier Transform-Infrared Spectroscopy (FT-IR), and confocal microscopy. The formation of smooth, continuous, and uniform nanofibers was observed and the addition of PEG resulted in an increase whereas the incorporation of DOX into nanofibers had no significant change in the diameter of nanofibers. Crosslinking also enlarged the diameter of all nanofibers and the most dramatic increase was observed 53% by DOX@PEGylated-gel. Afterward, the biological performance of the nanofibers was investigated by drug release profile, cytotoxicity on A549 cell line as well as antimicrobial activity with E. coli and S. aureus. The results indicate an enhanced drug release profile, moderate antimicrobial activity, and reasonable cytotoxic efficiency for thermally cross-linked nanofibers compared to uncross-linked nanofibers.Article Citation - WoS: 11Citation - Scopus: 13Effect of Cnt Incorporation on Pan/Ppy Nanofibers Synthesized by Electrospinning Method(TÜBİTAK, 2020) İnce Yardımcı, Atike; Tanoğlu, Metin; Yılmaz, Selahattin; Selamet, YusufIn this study, carbon nanotubes (CNTs) added polyacrylonitrile/polypyrrole (PAN/PPy) electrospun nanofibers were produced. Average diameters of the nanofibers were measured as 268 and 153 nm for 10 and 25 wt% of PPy contents, respectively. A relatively higher strain to failure values (23.3%) were observed for the low PPy content. When as-grown CNTs (1 and 4 wt%) were added into the PAN/PPy blends, disordered nanofibers were observed to form within the microstructure. To improve the interfacial properties of CNTs/PAN/PPy composites, CNTs were functionalized with H2SO4/HNO3/HCl solution. The functionalized CNTs were well dispersed within the nanofibers and aligned along the direction of nanofibers. Therefore, beads formation on nanofibers decreased. The impedance of the nanofibers was found to decrease with the PPy content and CNT addition. These nanofibers had a great potential to be used as an electrochemical actuator or a tissue engineering scaffold.