PubMed İndeksli Yayınlar Koleksiyonu / PubMed Indexed Publications Collection
Permanent URI for this collectionhttps://hdl.handle.net/11147/7645
Browse
7 results
Search Results
Now showing 1 - 7 of 7
Article Citation - WoS: 31Citation - Scopus: 36Integration of Triboluminescent Eud4tea Crystals To Transparent Polymers: Impact Sensor Application(American Chemical Society, 2017) İncel, Anıl; Eanes, Mehtap; McMillen, Colin D.; Demir, Mustafa MuammerLanthanide-based organometallic materials are well-known candidate triboluminescent (TL) materials that can show bright emission when a mechanical force is applied. These materials are usually in the form of crystalline powders, and it is often useful to integrate these samples into a polymer matrix in order to achieve processability, enabling coating from a solution/molten state or fabrication as a complex-shaped matrix. In this work, micrometer-sized europium tetrakis (dibenzoylmethide) triethylammonium (EuD4TEA) crystals were synthesized and integrated with various transparent polymers (PMMA, PS, PVDF, and PU) using two approaches: (i) blending and (ii) surface impregnation. In the former method, the crystalline particles were molecularly dissolved; therefore, a TL response cannot be achieved. More than 10 wt % TL crystals in the composite is needed to obtain TL signals. However, TL signal was achieved at 2.5 wt % when a composite was prepared by the latter approach. TL intensity shows exponential decay with consecutive mechanical action. The TL emission of PU-based surface impregnated composite expires with long-lived emission, and maximum TL response with respect to applied force was measured between 2.45 and 42.0 N.Article Citation - WoS: 64Citation - Scopus: 67Hierarchically Structured Metal Oxide/Silica Nanofibers by Colloid Electrospinning(American Chemical Society, 2012) Horzum Polat, Nesrin; Mun˜oz-Espí, Rafael; Glasser, Gunnar; Demir, Mustafa Muammer; Landfester, Katharina; Crespy, DanielWe present herein a new concept for the preparation of nanofibrous metal oxides based on the simultaneous electrospinning of metal oxide precursors and silica nanoparticles. Precursor fibers are prepared by electrospinning silica nanoparticles (20 nm in diameter) dispersed in an aqueous solution of poly(acrylic acid) and metal salts. Upon calcination in air, the poly(acrylic acid) matrix is removed, the silica nanoparticles are cemented, and nanocrystalline metal oxide particles of 4-14 nm are nucleated at the surface of the silica nanoparticles. The obtained continuous silica fibers act as a structural framework for metal oxide nanoparticles and show improved mechanical integrity compared to the neat metal oxide fibers. The hierarchically nanostructured materials are promising for catalysis applications, as demonstrated by the successful degradation of a model dye in the presence of the fibers.Article Citation - WoS: 73Citation - Scopus: 73Toward Transparent Nanocomposites Based on Polystyrene Matrix and Pmma-Grafted Ceo 2 Nanoparticles(American Chemical Society, 2011) Parlak, Onur; Demir, Mustafa MuammerThe association of transparent polymer and nanosized pigment particles offers attractive optical materials for various potential and existing applications. However, the particles embedded into polymers scatter light due to refractive index (RI) mismatch and reduce transparency of the resulting composite material. In this study, optical composites based on polystyrene (PS) matrix and poly(methyl methacrylate) (PMMA)-grafted CeO 2 hybrid particles were prepared. CeO 2 nanoparticles with an average diameter of 18 ± 8 nm were precipitated by treating Ce(NO 3) ·6H 2O with urea in the presence of a polymerizable surfactant, 3-methacyloxypropyltrimethoxy silane. PMMA chains were grafted on the surface of the nanoparticles upon free radical in situ solution polymerization. While blending of unmodified CeO 2 particles with PS resulted in opaque films, the transparency of the composite films was remarkably enhanced when prepared by PMMA-grafted CeO 2 hybrid particles, particularly those having a PMMA thickness of 9 nm. The improvement in transparency is presumably due to the reduction in RI mismatch between CeO 2 particles and the PS matrix when using PMMA chains at the interface.Article Citation - WoS: 22Citation - Scopus: 25Null Extinction of Ceria@silica Hybrid Particles: Transparent Polystyrene Composites(American Chemical Society, 2015) İncel, Anıl; Güner, Tuğrul; Parlak, Onur; Demir, Mustafa MustafaScattering of light in optical materials, particularly in composites based on transparent polymer and inorganic pigment nanoparticles, is a chronic problem. It might originate mainly from light scattering because of a refractive index mismatch between the particles and transparent polymer matrix. Thus, the intensity of light is rapidly diminished and optical transparency is reduced. Refractive index matching between the pigment core and the surrounding transparent matrix using a secondary component at the interface (shell) has recently appeared as a promising approach to alter light scattering. Here, CeO2 (ceria) nanoparticles with a diameter of 25 nm are coated with a SiO2 (silica) shell with various thicknesses in a range of 6.5-67.5 nm using the Stöber method. When the hybrid core-shell particles are dispersed into transparent polystyrene (PS), the transmission of the freestanding PS composite films increases over both the ultraviolet (UV) and visible region as the shell thickness increases particularly at 37.5 nm. The increase of transmission can be attributed to the reduction in the scattering coefficient of the hybrid particles. On the other hand, the particles in tetrahydrofuran (THF) absorb over UV and the intensity of absorption shows a systematic decrease as the shell thickness increases. Thus, the silica shell suppresses not only the scattering coefficient but also the molar absorptivity of the core ceria particles. The experimental results regarding the target shell thickness to develop low extinction (scattering + absorption) composites show a qualitative agreement with the predictions of Effective Medium Theory.Article Citation - WoS: 22Citation - Scopus: 28Mechanical Interlocking Between Porous Electrospun Polystyrene Fibers and an Epoxy Matrix(American Chemical Society, 2014) Demir, Mustafa Muammer; Horzum, Nesrin; Taşdemirci, Alper; Turan, Ali Kıvanç; Güden, MustafaAn epoxy matrix filled with nonwoven mats of porous polystyrene (PS) fibers processed by an electrospinning was compression tested at quasi-static (1 × 10–3 s–1) and high strain (315 s–1) rates. The electrospun PS fibers with a diameter between 6 and 9 μm, accommodated spherical pores on the surface with the sizes ranging from 0.1 to 0.2 μm. The filling epoxy matrix with 0.2 wt % PS fibers increased the compressive elastic modulus and compressive strength over those of neat epoxy resin. The microscopic observations indicated that the surface pores facilitated the resin intrusions into the fiber, enhancing the interlocking between resin and fibers, and increased the deformation energy expenditure of the polymer matrix.Article Citation - WoS: 70Citation - Scopus: 82Sorption Efficiency of Chitosan Nanofibers Toward Metal Ions at Low Concentrations(American Chemical Society, 2010) Horzum Polat, Nesrin; Boyacı, Ezel; Eroğlu, Ahmet Emin; Shahwan, Talal; Demir, Mustafa MuammerChitosan fibers showing narrow diameter distribution with a mean of 42 nm were produced by electrospinning and utilized for the sorption of Fe(III), Cu(II), Ag(I), and Cd(II) ions from aqueous solutions. The ion concentrations in the supernatant solutions were determined using inductively coupled plasma-mass spectrometry (ICP-MS). The filtration efficiency of the fibers toward these ions was studied by both batch and microcolumn methods. High efficiency in sorption of the metal ions was obtained in the both methods. The effects of sorbent amount (0.10−0.50 mg), shaking time (15−120 min), initial metal ion concentration (10.0−1000.0 μg·L−1), and temperature (25 and 50 °C) on the extent of sorption were examined. The sorbent amount did not significantly alter the efficiency of sorption; however, shaking time, temperature, and metal ion concentration were found to have a strong influence on sorption. By virtue of its mechanical integrity, the applicability of the chitosan mat in solid phase extraction under continuous flow looks promising.Article Citation - WoS: 28Citation - Scopus: 29Formation of Pseudoisocyanine J-Aggregates in Poly(vinyl Alcohol) Fibers by Electrospinning(American Chemical Society, 2009) Demir, Mustafa Muammer; Özen, Bengisu; Özçelik, SerdarSubmicrometer diameter, light emitting fibers of poly(vinyl alcohol) (PVA) doped with pseudoisocyanine (1,1′-diethyl-2,2′-cyanine bromide, PIC) dye were prepared by electrospinning. A horizontal setup was employed with a stationary collector consisting of two parallel-positioned metal strips separated by a void gap. Formation of uniaxially aligned and randomly deposited fibers in electrospun films was confirmed by microscopy. Photoluminescence (PL) spectroscopy is used to evaluate spectral properties of both types of fibers doped with PIC. While PIC molecules were individually dispersed in PVA solution, they assemble into J-aggregates upon electrospinning when the weight fraction of PIC molecules is above 2.5 wt %. The formation of J-aggregates was observed in both randomly deposited and uniaxially aligned electrospun fibers. Moreover, the fibers aligned uniaxially showed a high degree of polarized emission (PL |/PL⊥)10), arising from the orientation of J-aggregates along the fiber axis. On the other hand, isotropic emission of J-aggregates was observed from the fibers deposited randomly. As a conclusion, electrospinning was found to be an efficient and a practical method to form highly oriented J-aggregates dispersed into polymer fibers. To the best of our knowledge, it is the first time formation of J-aggregates (a bottom-up approach) and electrospinning (a topdown approach) is successfully combined.