Valorization of Olive Tree Pruning Waste for Potential Utilization in Lithium Recovery From Aqueous Solutions

Abstract

Olive tree pruning waste, mainly composed of olive branches, was converted into a value-added and sustainable product capable of lithium as a biosorbent through alkali treatment and phosphorylation reaction. Characterization studies were performed by SEM–EDX, XPS, FTIR, and TGA. Factors affecting biosorption mechanism, i.e., sorbent dosage, pH, initial Li+ concentration and temperature, and competitive ions’ presence, were investigated the synthesized functionalized olive branches (FOB). A commercial lithium selective resin, Lewatit TP 260, was also compared with FOB in batch and column studies. The Freundlich model fits adsorption isotherms better than the Langmuir model, with a maximum adsorption capacity of 6.7 mg/g at 30 °C and pH 7–8. Kinetic studies proved fast kinetics and equilibrium were attained in 6 min, while thermodynamic studies showed an exothermic (Δ Ho= - 17.52 kJ/ mol) , spontaneous reaction Δ Go< 0 at all temperatures), and increased randomness Δ So= + 24.27 J/ mol. K) at the interaction interface. Column studies revealed that although Lewatit TP 260 resin showed higher sorption capacity, its desorption efficiency (50.42%) was lower than that of FOB (99.9%), and the degree of column utilization of FOB (56.81%) was better than Lewatit TP 260 resin’s (16.0%). The findings were encouraging in the successful synthesis of a promising biosorbent from an abundant waste in Turkey for use in sustainable lithium recovery from aqueous sources. Graphical abstract: [Figure not available: see fulltext.]